SAE J403 Grade 1074
Equivalent material: DIN 1.9614, DIN SAE 1074, AISI 1074, EN 1.9614, ASTM Grade 1074, UNS G10740, DIN 1.0614, DIN D 75-2, DIN C76D, AFNOR C76D, BS C76D, AISI 1075, SAE 1075, JIS SWRH77B, JIS CS75, EN C76D, EN 1.0614, ISO C76D, GOST 75, GB C76D, GB U53762, GB/T C76D, GB/T U53762, UNS G10750, DIN 1.1248, DIN Ck75, DIN C75S, AFNOR C75S, AFNOR C75RR, AFNOR XC75, BS 70CS, BS 70HS, BS 060A78, BS C75S, BS CS70, BS 80, AISI 1070, AISI 1078, SAE 1070, SAE 1078, JIS S75CM, EN C75S, EN 1.1248, ISO CS75, GOST 75A, GB/T 75, GB/T U20752, ASTM Grade 1070M, UNS G10700, UNS G10780, DIN 1.1252, DIN D 78-3, DIN C78D2, AFNOR C78D2, BS C78D2, JIS SWRS77, EN C78D2, EN 1.1252, ISO C78D2, GB/T YL77, GB/T U53777, GB/T U53778, GB/T C78D2, DIN 1.1253, DIN D 75-3, DIN C76D2, AFNOR C76D2, BS C76D2, JIS SWRS75, EN C76D2, EN 1.1253, ISO C76D2, GB/T C76D2, DIN 1.0605, DIN C75, AFNOR C75, BS 80CS, BS 80HS, EN 42, EN 1.0605, IS 80C6
SAE J403 Grade 1074 general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for High Carbon Steel |
SAE J403 Grade 1074 thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 1/K |
Typical for High Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1289 - 1478 °C |
Typical for High Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 486 J/(kg·K) |
Typical for High Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 36 W/(m·K) |
Typical for High Carbon Steel |
SAE J403 Grade 1074 chemical
| Property |
Value |
| Aluminium |
Aluminium of 0.02 % |
| Carbon |
Carbon of 0.7 - 0.8 % |
| Chromium |
Chromium of 0.02 % |
| Copper |
Copper of 0.02 % |
| Iron |
balance |
| Manganese |
Manganese of 0.5 - 0.8 % |
| Molybdenum |
Molybdenum of 0.02 % |
| Nickel |
Nickel of 0.02 % |
| Niobium |
Niobium of 0.08 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.02 % |
| Sulfur |
Sulfur of 0.035 % |
| Titanium |
Titanium of 0.08 % |
| Vanadium |
Vanadium of 0.08 % |
SAE J403 Grade 1074 electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
SAE J403 Grade 1074 mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for High Carbon Steel |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for High Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 81 GPa |
Typical for High Carbon Steel |
Our steel products are meticulously tested and inspected to ensure utmost reliability.