ISO 16120-2 Grade C76D
ISO 16120-2 Grade C76D introduction
Non-alloy steel wire rod for drawing and/or cold rolling for general purpose wire rod (e.g. application for springs, steel wire).
Equivalent material: GB C76D, GB U53762, IS IS1835, IS IS7904, ISO C76D, ASTM A510 Grade 1074, ASTM A510 Grade 1075, ASTM A830 Grade 1074, UNS G10740, UNS G10750, DIN D75-2, IS nan, ASTM 1074, ASTM 1075, SAE 1074, SAE 1075, DIN 1.0614, DIN D 75-2, DIN C76D, AFNOR C76D, BS C76D, AISI 1074, AISI 1075, JIS SWRH77B, JIS CS75, EN 1.0614, GOST 75, GB/T C76D, GB/T U53762, ASTM Grade 1074
ISO 16120-2 Grade C76D general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for High Carbon Steel |
ISO 16120-2 Grade C76D thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 1/K |
Typical for High Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1289 - 1478 °C |
Typical for High Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 486 J/(kg·K) |
Typical for High Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 36 W/(m·K) |
Typical for High Carbon Steel |
ISO 16120-2 Grade C76D chemical
| Property |
Value |
| Aluminium |
Aluminium of 0.01 % |
| Carbon |
Carbon of 0.73 - 0.78 % |
| Chromium |
Chromium of 0.15 % |
| Copper |
Copper of 0.25 % |
| Manganese |
Manganese of 0.5 - 0.8 % |
| Molybdenum |
Molybdenum of 0.05 % |
| Nickel |
Nickel of 0.2 % |
| Phosphorus |
Phosphorus of 0.03 - 0.04 % |
| Silicon |
Silicon of 0.1 - 0.3 % |
| Sulfur |
Sulfur of 0.03 - 0.035 % |
ISO 16120-2 Grade C76D electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
ISO 16120-2 Grade C76D mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for High Carbon Steel |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for High Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 81 GPa |
Typical for High Carbon Steel |