SAE J403 Grade 1025
Equivalent material: DIN 1.0406, DIN C25, AFNOR C25, BS C25, AISI 1025, EN C25, EN 1.0406, ISO C25, GB/T 25, GB/T U20252, ASTM M1025, ASTM Grade 1025, UNS G10250, DIN 1.0415, DIN D 25-2, DIN C26D, AFNOR C26D, BS C26D, JIS SWRH27, JIS STKN400W, EN C26D, EN 1.0415, GB/T C26D, GB/T U53262, DIN 1.1139, DIN C26D2, AFNOR C26D2, BS C26D2, EN C26D2, EN 1.1139, ISO C26D2, GB/T C26D2, DIN 1.1158, DIN Ck25, DIN C25E, AFNOR XC25, AFNOR C25E, BS 070M26, BS C25E, UNI C25, JIS S25C, JIS S28C, EN C25E, EN 1.1158, ISO C25E4, ISO C25E, ISO S25C, GOST 25, GB/T U20252, GB/T ML25, GB/T U40252, DIN 1.1163, DIN C25R, DIN Cm 25, EN C25R, EN 1.1163, ISO C25R, ISO C25M2, JIS SWRCH25K, ASTM 1025, ASTM Grade SC1025
SAE J403 Grade 1025 general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
SAE J403 Grade 1025 thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
SAE J403 Grade 1025 chemical
| Property |
Value |
| Aluminium |
Aluminium of 0.02 % |
| Carbon |
Carbon of 0.22 - 0.28 % |
| Chromium |
Chromium of 0.02 % |
| Copper |
Copper of 0.02 % |
| Iron |
balance |
| Manganese |
Manganese of 0.3 - 0.6 % |
| Molybdenum |
Molybdenum of 0.02 % |
| Nickel |
Nickel of 0.02 % |
| Niobium |
Niobium of 0.08 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.02 % |
| Sulfur |
Sulfur of 0.035 % |
| Titanium |
Titanium of 0.08 % |
| Vanadium |
Vanadium of 0.08 % |
SAE J403 Grade 1025 magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
SAE J403 Grade 1025 electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
SAE J403 Grade 1025 mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |