SAE J403 Grade 1017
Equivalent material: DIN 1.0416, DIN C18D, AFNOR C18D, BS C18D, AISI 1017, JIS SWRM17, JIS S17C, EN C18D, EN 1.0416, ISO C18D, GB/T C18D, GB/T U53182, ASTM M1017, ASTM Grade 1017, UNS G10170, DIN 1.0401, DIN St 37-2, DIN St 37-2 G, DIN St 37, DIN St37-2, DIN C15, AFNOR CC12, BS 080M15, UNI C15C16, SS 1350, UNE F.111, AISI 1015, AISI 1016, SAE 1015, SAE 1016, JIS S15C, EN C15, EN 1.0401, ASTM M1015, ASTM Grade 1015, UNS G10150, DIN 1.1141, DIN Ck15, DIN C15E, AFNOR C15E, AFNOR XC18, AFNOR C18RR, AFNOR XC15, BS C15E, BS En32C, BS 080A15, UNI C16, SS 1370, UNE C15K, JIS S15CK, EN C15E, EN 1.1141, ISO C15E4, ISO C15E, ISO S15C, GOST 15, GB/T 15, GB/T U20152
SAE J403 Grade 1017 general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
SAE J403 Grade 1017 thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
SAE J403 Grade 1017 chemical
| Property |
Value |
| Aluminium |
Aluminium of 0.02 % |
| Carbon |
Carbon of 0.15 - 0.2 % |
| Chromium |
Chromium of 0.02 % |
| Copper |
Copper of 0.02 % |
| Iron |
balance |
| Manganese |
Manganese of 0.3 - 0.6 % |
| Molybdenum |
Molybdenum of 0.02 % |
| Nickel |
Nickel of 0.02 % |
| Niobium |
Niobium of 0.08 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.02 % |
| Sulfur |
Sulfur of 0.035 % |
| Titanium |
Titanium of 0.08 % |
| Vanadium |
Vanadium of 0.08 % |
SAE J403 Grade 1017 magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
SAE J403 Grade 1017 electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
SAE J403 Grade 1017 mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |