EN 10277-2 Grade St 37-2 turned
EN 10277-2 Grade St 37-2 turned introduction
St 37-2 is used for moderate loaded parts, without inspection.
Equivalent material: GOST S255, ISO Fe360-B, JIS SN400C, DIN 1.0401, DIN St 37-2 G, DIN St 37, DIN St37-2, DIN C15, AFNOR CC12, BS 080M15, UNI C15C16, SS 1350, UNE F.111, AISI 1015, AISI 1017, AISI 1016, SAE 1015, SAE 1017, SAE 1016, JIS S15C, EN C15, EN 1.0401, ASTM M1015, ASTM Grade 1015, UNS G10150, UNS G10170
EN 10277-2 Grade St 37-2 turned general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.85 g/cm³ |
EN 10277-2 Grade St 37-2 turned thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
-100.0 °C |
Coefficient of thermal expansion of 1.08E-5 1/K |
- |
| - |
20.0 °C |
Coefficient of thermal expansion of 1.19E-5 1/K |
- |
| - |
100.0 °C |
Coefficient of thermal expansion of 1.25E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.3E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.36E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.41E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.45E-5 1/K |
- |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.49E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
-100.0 °C |
Specific heat capacity of 423 J/(kg·K) |
- |
| - |
20.0 °C |
Specific heat capacity of 461 J/(kg·K) |
- |
| - |
100.0 °C |
Specific heat capacity of 479 J/(kg·K) |
- |
| - |
200.0 °C |
Specific heat capacity of 499 J/(kg·K) |
- |
| - |
300.0 °C |
Specific heat capacity of 517 J/(kg·K) |
- |
| - |
400.0 °C |
Specific heat capacity of 536 J/(kg·K) |
- |
| - |
500.0 °C |
Specific heat capacity of 558 J/(kg·K) |
- |
| - |
600.0 °C |
Specific heat capacity of 587 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 56.9 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 56.4 W/(m·K) |
- |
| - |
200.0 °C |
Thermal conductivity of 53.5 W/(m·K) |
- |
| - |
300.0 °C |
Thermal conductivity of 49.4 W/(m·K) |
- |
| - |
400.0 °C |
Thermal conductivity of 45.2 W/(m·K) |
- |
| - |
500.0 °C |
Thermal conductivity of 41.3 W/(m·K) |
- |
| - |
600.0 °C |
Thermal conductivity of 37.6 W/(m·K) |
- |
| Thermal diffusivity |
20.0 °C |
Thermal diffusivity of 15.7 mm²/s |
- |
| - |
100.0 °C |
Thermal diffusivity of 14.5 mm²/s |
- |
| - |
200.0 °C |
Thermal diffusivity of 12.9 mm²/s |
- |
| - |
300.0 °C |
Thermal diffusivity of 11.2 mm²/s |
- |
| - |
400.0 °C |
Thermal diffusivity of 9.6 mm²/s |
- |
| - |
500.0 °C |
Thermal diffusivity of 7.9 mm²/s |
- |
| - |
600.0 °C |
Thermal diffusivity of 6.3 mm²/s |
- |
EN 10277-2 Grade St 37-2 turned chemical
| Property |
Value |
| Carbon |
Carbon of 0.2 % |
| Phosphorus |
Phosphorus of 0.05 % |
| Sulfur |
Sulfur of 0.05 % |
EN 10277-2 Grade St 37-2 turned magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
EN 10277-2 Grade St 37-2 turned electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 1.83E-7 Ω·m |
| - |
100.0 °C |
Electrical resistivity of 2.27E-7 Ω·m |
| - |
200.0 °C |
Electrical resistivity of 2.95E-7 Ω·m |
| - |
300.0 °C |
Electrical resistivity of 3.8E-7 Ω·m |
| - |
400.0 °C |
Electrical resistivity of 4.81E-7 Ω·m |
| - |
500.0 °C |
Electrical resistivity of 5.99E-7 Ω·m |
| - |
600.0 °C |
Electrical resistivity of 7.38E-7 Ω·m |
EN 10277-2 Grade St 37-2 turned mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
-100.0 °C |
Elastic modulus of 217 GPa |
- |
| - |
20.0 °C |
Elastic modulus of 212 GPa |
- |
| - |
100.0 °C |
Elastic modulus of 207 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 199 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 192 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 184 GPa |
- |
| - |
500.0 °C |
Elastic modulus of 175 GPa |
- |
| - |
600.0 °C |
Elastic modulus of 164 GPa |
- |
| Elongation |
20.0 °C |
Elongation of 22 - 24 % |
- |
| Poisson's ratio |
20.0 °C |
Poisson's ratio of 0.28 [-] |
- |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 340 - 470 MPa |
- |
| Yield strength |
20.0 °C |
Yield strength of 215 - 225 MPa |
- |
Let our innovative steel solutions unleash your creativity and drive excellence in your industry.
-- Our promise