BS 970-1 Grade 080M15
BS 970-1 Grade 080M15 introduction
080M15(EN32) has a good wear resistance and it is suitable for applications that require light stress forces. It can be case hardened and has good machinability and weldability.
Equivalent material: DIN CK15, IS C14, EN EN32B, SAE 1015, SAE 1016, SAE 1018, IS C15Mn75, Din 1.1141, DIN 1.0401, DIN St 37-2, DIN St 37-2 G, DIN St 37, DIN St37-2, DIN C15, AFNOR CC12, UNI C15C16, SS 1350, UNE F.111, AISI 1015, AISI 1017, AISI 1016, SAE 1015, SAE 1017, SAE 1016, JIS S15C, EN C15, EN 1.0401, ASTM M1015, ASTM Grade 1015, UNS G10150, UNS G10170, DIN 1.1141, DIN Ck15, DIN C15E, AFNOR C15E, AFNOR XC18, AFNOR C18RR, AFNOR XC15, BS C15E, BS En32C, BS 080A15, UNI C16, SS 1370, UNE C15K, JIS S15CK, EN C15E, EN 1.1141, ISO C15E4, ISO C15E, ISO S15C, GOST 15, GB/T 15, GB/T U20152, DIN 1.1148, DIN Ck15Al, DIN C16E, AFNOR C16E, BS C16E, BS S14, BS 4S14, EN C16E, EN 1.1148, ISO C16E, ISO C16E4, GB/T 15AI, GB/T U22152, ASTM Grade 1016, UNS G10160
BS 970-1 Grade 080M15 general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
BS 970-1 Grade 080M15 thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
BS 970-1 Grade 080M15 chemical
| Property |
Value |
| Carbon |
Carbon of 0.1 - 0.18 % |
| Manganese |
Manganese of 1 % |
| Phosphorus |
Phosphorus of 0.05 % |
| Silicon |
Silicon of 0.35 % |
| Sulfur |
Sulfur of 0.05 % |
BS 970-1 Grade 080M15 magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
BS 970-1 Grade 080M15 electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
BS 970-1 Grade 080M15 mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Elongation A50 |
23.0 °C |
Elongation A50 of 18 % |
blank case hardened |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 430 MPa |
blank case hardened |