SAE HNV-6
Equivalent material: DIN 1.4747, DIN X80CrNiSi20, AFNOR Z80CSN20-02, BS 443S65, UNI X80CrSiNi20, UNE F.320B, AISI HNV-6, SAE HNV-6, JIS SUH4, EN 1.4747, UNS S65006
SAE HNV-6 general
| Property |
Temperature |
Value |
Comment |
| Density |
20.0 °C |
Density of 7.4 - 7.7 g/cm³ |
Typical for Martensitic Stainless Steel |
SAE HNV-6 thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
200.0 °C |
Coefficient of thermal expansion of 9.8E-6 1/K |
The mentioned values are between 20°C and the mentioned temperature |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.15E-5 1/K |
The mentioned values are between 20°C and the mentioned temperature |
| - |
1000.0 °C |
Coefficient of thermal expansion of 1.24E-5 1/K |
The mentioned values are between 20°C and the mentioned temperature |
| - |
1300.0 °C |
Coefficient of thermal expansion of 1.31E-5 1/K |
The mentioned values are between 20°C and the mentioned temperature |
| Melting point |
- |
Melting point of 1375 - 1450 °C |
Typical for Martensitic Stainless Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 460 J/(kg·K) |
Typical for Martensitic Stainless Steel |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 14 - 31 W/(m·K) |
Typical for Martensitic Stainless Steel |
SAE HNV-6 chemical
| Property |
Value |
| Carbon |
Carbon of 0.75 - 0.9 % |
| Chromium |
Chromium of 19 - 21 % |
| Iron |
Balance |
| Manganese |
Manganese of 0.8 % |
| Nickel |
Nickel of 1 - 1.7 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 1.75 - 2.6 % |
| Sulfur |
Sulfur of 0.04 % |
SAE HNV-6 electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 6E-7 Ω·m |
Typical for Martensitic Stainless Steel |
SAE HNV-6 mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 194 - 220 GPa |
Typical for Martensitic Stainless Steel |
| Elongation A5 |
20.0 °C |
Elongation A5 of 8 - 15.5 % |
- |
| Hardness, Brinell |
20.0 °C |
Hardness, Brinell of 293 [-] |
- |
| Poisson's ratio |
20.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Martensitic Stainless Steel |
| Reduction of area |
20.0 °C |
Reduction of area of 9 - 10 % |
- |
| Tensile strength |
20.0 °C |
Tensile strength of 940 - 941 MPa |
- |
| Yield strength |
20.0 °C |
Yield strength of 840 - 844 MPa |
- |