JIS G5111 Grade SCMn1A
Equivalent material: GOST 20G2, AS KX1320, AS X1320H, BS A, BS 175H23, IS 20Mn2, IS St55, UNE F.120.L, UNE 20Mn6-1, UNE AM22Mn5, ASTM 1524, MIL 5, MIL 6, JIS SWRCH24K, JIS SMn420H, JIS SMn420, AISI 1524, SAE 1524, ASTM 1524H, AISI 1524H, SAE 1524H, DIN 1.1170, DIN 28Mn6, DIN ETG 25, AFNOR 28Mn6, AFNOR 20M5, BS 26Mn6, BS En14A, BS En14B, BS 150M19, AISI 1330H, AISI 1527, AISI 1330, SAE 1330H, SAE 1527, SAE 1330, JIS S33C, JIS SCMn1B, JIS SCMn1, EN 28Mn6, EN 1.1170, ISO 28Mn6, GOST 30G2, GB 30Mn2, GB A00302, GB/T 30Mn2, GB/T A00302, UNS H13300, UNS G13300, IS 20C15
JIS G5111 Grade SCMn1A general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Manganese Steel |
JIS G5111 Grade SCMn1A thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.33E-5 1/K |
Typical for Manganese Steel |
| Melting point |
- |
Melting point of 1382 - 1529 °C |
Typical for Manganese Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 510 - 553 J/(kg·K) |
Typical for Manganese Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 14 - 16 W/(m·K) |
Typical for Manganese Steel |
JIS G5111 Grade SCMn1A mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Manganese Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 17 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 143 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Manganese Steel |
| Reduction of area |
23.0 °C |
Reduction of area of 35 % |
- |
| Tensile strength |
23.0 °C |
Tensile strength of 540 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 275 MPa |
- |
Optimize your operations and streamline productivity with our efficient steel solutions.