ASTM A513 Grade 1524 DOM Stress-Relieved
Equivalent material: AISI 1524, SAE 1524, JIS SWRCH24K, UNS G15240, DIN 1.1160, DIN 22Mn6, BS 150M19, AISI 1524H, SAE 1524H, JIS SMn420, EN 1.1160, ISO 22Mn6, GOST 20G2, UNS H15240
ASTM A513 Grade 1524 DOM Stress-Relieved general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
ASTM A513 Grade 1524 DOM Stress-Relieved thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
ASTM A513 Grade 1524 DOM Stress-Relieved chemical
| Property |
Value |
| Carbon |
Carbon of 0.19 - 0.25 % |
| Manganese |
Manganese of 1.35 - 1.65 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Sulfur |
Sulfur of 0.05 % |
ASTM A513 Grade 1524 DOM Stress-Relieved magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
ASTM A513 Grade 1524 DOM Stress-Relieved electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
ASTM A513 Grade 1524 DOM Stress-Relieved mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Elongation A50 |
23.0 °C |
Elongation A50 of 10 % |
- |
| Hardness, Rockwell B |
23.0 °C |
Hardness, Rockwell B of 85 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 585 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 515 MPa |
- |
Conquer challenging environments with confidence using our durable steel products, engineered to withstand extreme conditions.