JIS G4804 Grade 11SMn28 cold-drawn
Equivalent material: DIN 1.0715, DIN 9SMn28, DIN 11SMn30, AFNOR S250, AFNOR 11SMn30, BS 230M07, BS 11SMN30, BS 220M07, UNI CF9SMn28, UNI 9SMn23, SS 1912, UNE 11SMn28, AISI 1213, AISI 1215, SAE 1213, SAE 1215, JIS SUM22, JIS SUM23, EN 11SMn30, EN 1.0715, ISO 11SMn28, ISO 11SMn30, GB/T U71152, GB/T Y15, UNS G12130, UNS G12150
JIS G4804 Grade 11SMn28 cold-drawn general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
JIS G4804 Grade 11SMn28 cold-drawn thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
JIS G4804 Grade 11SMn28 cold-drawn magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
JIS G4804 Grade 11SMn28 cold-drawn electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
JIS G4804 Grade 11SMn28 cold-drawn mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 7 - 10 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 380 - 810 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 245 - 410 MPa |
- |