JIS G4802 Grade CS60 full hard
Equivalent material: DIN 1.0610, DIN D 60-2, DIN C60D, AFNOR C60D, BS C60D, AISI 1060, SAE 1060, EN C60D, EN 1.0610, ISO C60D, GB/T C60D, GB/T U53602, ASTM 1060, UNS G10600
JIS G4802 Grade CS60 full hard general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for High Carbon Steel |
JIS G4802 Grade CS60 full hard thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 1/K |
Typical for High Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1289 - 1478 °C |
Typical for High Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 486 J/(kg·K) |
Typical for High Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 36 W/(m·K) |
Typical for High Carbon Steel |
JIS G4802 Grade CS60 full hard electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
JIS G4802 Grade CS60 full hard mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for High Carbon Steel |
| Hardness, Rockwell B |
23.0 °C |
Hardness, Rockwell B of 98 [-] |
- |
| Hardness, Rockwell Superficial 15-T |
23.0 °C |
Hardness, Rockwell Superficial 15-T of 92 [-] |
- |
| Hardness, Rockwell Superficial 30-T |
23.0 °C |
Hardness, Rockwell Superficial 30-T of 83 [-] |
- |
| Hardness, Vickers |
23.0 °C |
Hardness, Vickers of 230 - 250 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for High Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 81 GPa |
Typical for High Carbon Steel |
Our customized steel solutions ensure the perfect fit for your specific project requirements.
-- Our promise
Similar or equivalent steel materials
Get a quote