JIS G4317 Grade SUS304L
Equivalent material: DIN 1.4307, DIN G-X2CrNiN18-9, AFNOR Z3CN19-09, BS 304S11, SS 2352, AISI 304L, SAE 304L, EN X2CrNi18-9, EN 1.4307, GOST 03Ch18N11, GB 00Cr19Ni10, ASTM TP304L, UNS S30403, IS X02Cr18Ni11, DIN 1.4650, AISI 304LCu, SAE 304LCu, EN X2CrNiCu19-10, EN 1.4650, ASTM 304L, ASTM S30403, ASTM F304L, ASTM MT304L, DIN 1.4306, DIN X2CrNi19-11, DIN 19Cr11Ni, AFNOR Z3CN18-10, JIS SCS19, JIS SCS19A, JIS SUS304LTB, JIS SUS304LTP, JIS SUS304LTPY, JIS SUS304LTBS, JIS SUSF304L, EN X2CrNi19-11, EN 1.4306, ISO A3, ASTM Grade CPF3
JIS G4317 Grade SUS304L general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.9 - 8.2 g/cm³ |
Typical for Austenitic Stainless Steel |
JIS G4317 Grade SUS304L thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.7E-5 - 1.9E-5 1/K |
Typical for Austenitic Stainless Steel |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 440 J/(kg·K) |
Typical for Austenitic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 11 - 21 W/(m·K) |
Typical for Austenitic Stainless Steel |
JIS G4317 Grade SUS304L electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
JIS G4317 Grade SUS304L mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 195 GPa |
Typical for Austenitic Stainless Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 40 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 187 [-] |
- |
| Hardness, Rockwell B |
23.0 °C |
Hardness, Rockwell B of 90 [-] |
- |
| Hardness, Vickers |
23.0 °C |
Hardness, Vickers of 200 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 480 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 175 MPa |
- |
Our steel products are meticulously tested and inspected to ensure utmost reliability.