DIN 1654-5 Grade X2CrNi19-11 cold drawn, quenched and slightly skin passed introduction

The steel X 2 CrNi 19 11 is well suited for cold-forming. It is used for screws, nuts and molded parts in the chemical equipment industry, the food industry and in nuclear reactor technology. The steel can be high-gloss polished and can be used in temperatures of up to 400 degrees C.

Equivalent material: AFNOR Z2CN18-10, BS 304S11, GOST 03Ch18N11, ISO D20, UNI X2CrNi18-11, JIS SUS304L, PN 00H18N10, SS 2352, UNE F.3503-X2CrNi19-10, ASTM 304L, DIN 1.4306, DIN 19Cr11Ni, AFNOR Z3CN18-10, AISI 304L, SAE 304L, JIS SCS19, JIS SCS19A, JIS SUS304LTB, JIS SUS304LTP, JIS SUS304LTPY, JIS SUS304LTBS, JIS SUSF304L, EN X2CrNi19-11, EN 1.4306, ISO A3, GB 00Cr19Ni10, ASTM Grade CPF3, UNS S30403

DIN 1654-5 Grade X2CrNi19-11 cold drawn, quenched and slightly skin passed general

Property Temperature Value
Density 20.0 °C Density of 7.92 g/cm³

DIN 1654-5 Grade X2CrNi19-11 cold drawn, quenched and slightly skin passed thermal

Property Temperature Value Comment
Coefficient of thermal expansion -100.0 °C Coefficient of thermal expansion of 1.49E-5 1/K -
- 20.0 °C Coefficient of thermal expansion of 1.61E-5 1/K -
- 100.0 °C Coefficient of thermal expansion of 1.6E-5 - 1.67E-5 1/K -
- 200.0 °C Coefficient of thermal expansion of 1.7E-5 - 1.72E-5 1/K -
- 300.0 °C Coefficient of thermal expansion of 1.7E-5 - 1.77E-5 1/K -
- 400.0 °C Coefficient of thermal expansion of 1.8E-5 - 1.81E-5 1/K -
- 500.0 °C Coefficient of thermal expansion of 1.8E-5 - 1.84E-5 1/K -
- 600.0 °C Coefficient of thermal expansion of 1.88E-5 1/K -
- 700.0 °C Coefficient of thermal expansion of 1.91E-5 1/K -
- 800.0 °C Coefficient of thermal expansion of 1.94E-5 1/K -
Max service temperature, long - Max service temperature, long of 0 - 400 °C -
Melting point - Melting point of 1375 - 1450 °C Typical for Austenitic Stainless Steel
Specific heat capacity -100.0 °C Specific heat capacity of 440 J/(kg·K) -
- 20.0 °C Specific heat capacity of 472 J/(kg·K) -
- 100.0 °C Specific heat capacity of 487 J/(kg·K) -
- 200.0 °C Specific heat capacity of 503 J/(kg·K) -
- 300.0 °C Specific heat capacity of 512 J/(kg·K) -
- 400.0 °C Specific heat capacity of 520 J/(kg·K) -
- 500.0 °C Specific heat capacity of 530 J/(kg·K) -
- 600.0 °C Specific heat capacity of 541 J/(kg·K) -
- 700.0 °C Specific heat capacity of 551 J/(kg·K) -
- 800.0 °C Specific heat capacity of 559 J/(kg·K) -
Thermal conductivity 20.0 °C Thermal conductivity of 13.9 W/(m·K) -
- 100.0 °C Thermal conductivity of 15.4 W/(m·K) -
- 200.0 °C Thermal conductivity of 17.2 W/(m·K) -
- 300.0 °C Thermal conductivity of 18.7 W/(m·K) -
- 400.0 °C Thermal conductivity of 20.2 W/(m·K) -
- 500.0 °C Thermal conductivity of 21.6 W/(m·K) -
- 600.0 °C Thermal conductivity of 23 W/(m·K) -
- 700.0 °C Thermal conductivity of 24.4 W/(m·K) -
- 800.0 °C Thermal conductivity of 25.8 W/(m·K) -
Thermal diffusivity 20.0 °C Thermal diffusivity of 3.7 mm²/s -
- 100.0 °C Thermal diffusivity of 3.9 mm²/s -
- 200.0 °C Thermal diffusivity of 4.2 mm²/s -
- 300.0 °C Thermal diffusivity of 4.5 mm²/s -
- 400.0 °C Thermal diffusivity of 4.7 mm²/s -
- 500.0 °C Thermal diffusivity of 4.8 mm²/s -
- 600.0 °C Thermal diffusivity of 5 mm²/s -
- 700.0 °C Thermal diffusivity of 5.3 mm²/s -
- 800.0 °C Thermal diffusivity of 5.6 mm²/s -

DIN 1654-5 Grade X2CrNi19-11 cold drawn, quenched and slightly skin passed chemical

Property Value
Carbon Carbon of 0.03 %
Chromium Chromium of 18 - 20 %
Manganese Manganese of 2 %
Nickel Nickel of 10 - 12.5 %
Phosphorus Phosphorus of 0.05 %
Silicon Silicon of 1 %
Sulfur Sulfur of 0.03 %

DIN 1654-5 Grade X2CrNi19-11 cold drawn, quenched and slightly skin passed electrical

Property Temperature Value
Electrical resistivity 20.0 °C Electrical resistivity of 7.35E-7 Ω·m
- 100.0 °C Electrical resistivity of 8E-7 Ω·m
- 200.0 °C Electrical resistivity of 8.68E-7 Ω·m
- 300.0 °C Electrical resistivity of 9.33E-7 Ω·m
- 400.0 °C Electrical resistivity of 9.89E-7 Ω·m
- 500.0 °C Electrical resistivity of 1.04E-6 Ω·m
- 600.0 °C Electrical resistivity of 1.08E-6 Ω·m
- 700.0 °C Electrical resistivity of 1.12E-6 Ω·m
- 800.0 °C Electrical resistivity of 1.15E-6 Ω·m

DIN 1654-5 Grade X2CrNi19-11 cold drawn, quenched and slightly skin passed mechanical

Property Temperature Value
Elastic modulus -100.0 °C Elastic modulus of 206 GPa
- 20.0 °C Elastic modulus of 196 - 198.1 GPa
- 100.0 °C Elastic modulus of 190 - 194 GPa
- 200.0 °C Elastic modulus of 182 - 186 GPa
- 300.0 °C Elastic modulus of 174 - 179 GPa
- 400.0 °C Elastic modulus of 166 - 172 GPa
- 500.0 °C Elastic modulus of 158 - 165 GPa
- 600.0 °C Elastic modulus of 150 GPa
- 700.0 °C Elastic modulus of 142 GPa
- 800.0 °C Elastic modulus of 134 GPa
Poisson's ratio 20.0 °C Poisson's ratio of 0.29 [-]
Reduction of area 20.0 °C Reduction of area of 55 %
Shear modulus 20.0 °C Shear modulus of 75.7 GPa
Tensile strength 20.0 °C Tensile strength of 680 MPa