JIS G4309 Grade SUS430F
Equivalent material: GB/T 1Cr17, GB/T 1Cr17-Q, GB 1Cr17, GB 1Cr15, GB Y1Cr17, GOST 12Х17, GOST 12H17, AS 430, AS 430F, DIN X6Cr17, DIN X12CrMoS17, NF Z8C17, NF Z10CF17, NF Z13CF17, BS 430S15, BS 430S17, IS 05Cr17, IS 08Cr17, UNI X8Cr17, UNI X10CrS17, EN X6Cr17, UNE X8Cr17, UNE X10CrS17, UNE X6Cr17, UNE F.310.D, SIS 2383-02, SIS 2383-03, SIS 2320, SIS 2383, AMS 5503, AMS 5627, ASME 430, ASTM 430F, ASTM F430, ASTM TP430, ASTM MT430, ASTM WP430, ASTM 430, MIL 430, MIL 430F, JIS SUS430TB, JIS SUS430, AISI 430, AISI 430F, GB/T ML1Cr17, GB/T Y1Cr17, GB/T Y1Cr17-Q, EN X14CrMoS17, DIN 1.4104, AFNOR Z13CF17, BS 441S29, SS 2383, UNE F.3117, SAE 430F, EN 1.4104, ISO X14CrMoS17, ISO C4, GB Y10Cr17, UNS S43020, DIN 1.4105, DIN X 4 CrMoS 18, DIN X6CrMoS17, DIN X4CrMoS18, AFNOR Z8CF17, UNE F.3114, EN X6CrMoS17, EN 1.4105, ISO X6CrMoS17
JIS G4309 Grade SUS430F general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.6 - 7.7 g/cm³ |
Typical for Martensitic Stainless Steel |
JIS G4309 Grade SUS430F thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1E-5 - 1.5E-5 1/K |
Typical for Martensitic Stainless Steel |
| Melting point |
- |
Melting point of 1370 - 1530 °C |
Typical for Martensitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 460 J/(kg·K) |
Typical for Martensitic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 14 - 31 W/(m·K) |
Typical for Martensitic Stainless Steel |
JIS G4309 Grade SUS430F electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 6E-7 Ω·m |
Typical for Martensitic Stainless Steel |
JIS G4309 Grade SUS430F mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 220 GPa |
Typical for Martensitic Stainless Steel |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Martensitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Martensitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 590 - 930 MPa |
- |