JIS G4307 Grade SUS403
Equivalent material: GB 1Cr13, GB H0Cr14, GB H1Cr13, GB 0Cr13, GOST 08Х13, GOST 08H13, GOST 08H13-Sh, AS 410S, DIN X6Cr13, NF Z6C13, NF Z12C13M, NF Z8C12, NF Z13C13, NF Z8C13FF, NF Z15C13, BS 403S17, BS S.3S61, BS 420S29, IS 04Cr13, IS 6527, UNI X6Cr13, EN X6Cr13, UNE AM-X12Cr13, UNE X6Cr13, UNE X15Cr13, SIS 2301-02, SIS 2301-22, SIS 2301-23, SIS 2301, AMS 5611, AMS 5612, ASME 410S, ASTM 410S, ASTM 403, ASTM MT403, MIL 403, JIS SUS410S, JIS SUS429, JIS SUS410J1, AISI 403, AISI 410S, ASTM S41008, SAE 410S, GB/T 0Cr13, ASME 429, ASTM F429, ASTM TP429, ASTM MT429, ASTM WP429, ASTM 429, MIL 429, DIN 1.4000, AFNOR Z8C13FF, AFNOR Z8C12, AFNOR X6Cr13, BS X6Cr13, UNI X6Cr3, SS 2301, UNE F.3110, AISI S41008, AISI S40300, SAE S41008, SAE 403, SAE S40300, JIS SUS403FB, EN 1.4000, ISO 65, ISO X6Cr13, ISO 4000-410-08-I, ISO FP13G, GOST 08Ch13, GOST X6Cr13, GB/T 0Cr13, GB/T 06Cr13, GB/T S41008, UNS S41008, UNS S40300
JIS G4307 Grade SUS403 general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.6 - 7.7 g/cm³ |
Typical for Martensitic Stainless Steel |
JIS G4307 Grade SUS403 thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1E-5 - 1.5E-5 1/K |
Typical for Martensitic Stainless Steel |
| Melting point |
- |
Melting point of 1370 - 1530 °C |
Typical for Martensitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 460 J/(kg·K) |
Typical for Martensitic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 14 - 31 W/(m·K) |
Typical for Martensitic Stainless Steel |
JIS G4307 Grade SUS403 chemical
| Property |
Value |
| Carbon |
Carbon of 0.15 % |
| Chromium |
Chromium of 11.5 - 13 % |
| Iron |
Iron of 84.68 - 88.5 % |
| Manganese |
Manganese of 1 % |
| Nickel |
Nickel of 0.6 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 0.5 % |
| Sulfur |
Sulfur of 0.03 % |
JIS G4307 Grade SUS403 electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 6E-7 Ω·m |
Typical for Martensitic Stainless Steel |
JIS G4307 Grade SUS403 mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 220 GPa |
Typical for Martensitic Stainless Steel |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Martensitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Martensitic Stainless Steel |