JIS G4305 Grade SUS429 annealed
Equivalent material: GB H0Cr14, AS 410S, UNE AM-X12Cr13, ASME 429, ASTM TP429, ASTM 429, ASTM F429, ASTM MT429, ASTM WP429, MIL 429, AISI 429, SAE 429, GB 1Cr13, GB H1Cr13, GB 0Cr13, GOST 08Х13, GOST 08H13, GOST 08H13-Sh, DIN X6Cr13, NF Z6C13, NF Z12C13M, NF Z8C12, NF Z13C13, NF Z8C13FF, NF Z15C13, BS 403S17, BS S.3S61, BS 420S29, UNI X6Cr13, UNE X6Cr13, UNE X15Cr13, SIS 2301-02, SIS 2301-22, SIS 2301-23, SIS 2301, AMS 5611, AMS 5612, ASTM 403, ASTM MT403, MIL 403, JIS SUS403, JIS SUS410S, JIS SUS410J1, AISI 403, IS 04Cr13, IS 6527, ASME 410S, ASTM 410S, AISI 410S, ASTM S41008, SAE 410S, ASTM S42900, UNS S42900
JIS G4305 Grade SUS429 annealed general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.6 - 7.8 g/cm³ |
Typical for Ferritic Stainless Steel |
JIS G4305 Grade SUS429 annealed thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 9.3E-6 - 1.2E-5 1/K |
Typical for Ferritic Stainless Steel |
| Melting point |
- |
Melting point of 1425 - 1530 °C |
Typical for Ferritic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 420 - 586 J/(kg·K) |
Typical for Ferritic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 11 - 22 W/(m·K) |
Typical for Ferritic Stainless Steel |
JIS G4305 Grade SUS429 annealed electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 6E-7 - 7.5E-7 Ω·m |
Typical for Ferritic Stainless Steel |
JIS G4305 Grade SUS429 annealed mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 220 GPa |
Typical for Ferritic Stainless Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 22 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 183 [-] |
- |
| Hardness, Rockwell B |
23.0 °C |
Hardness, Rockwell B of 88 [-] |
- |
| Hardness, Vickers |
23.0 °C |
Hardness, Vickers of 200 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Ferritic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Ferritic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 450 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 205 MPa |
- |