JIS G4306 Grade SUS302 hot-rolled, solution annealed
Equivalent material: GOST 12Х18Н9, GOST 12H18N9, AS 302, NF Z10CN18-09, BS 302S25, BS 302S26, BS 302S31, UNI X10CrNi1809, UNE X10CrNi189, SIS 2332-02, AMS 5515, AMS 5516, AMS 5600, AMS 5636, AMS 5637, AMS 5688, AMS 5693, AMS 7210, AMS 7241, AMS 7472, ASME 302, ASTM 302, ASTM MT302, MIL 302, MIL S-5059, MIL S-7720, MIL S-862, AISI 302, SAE 302, JIS SUS302, UNS S30200, DIN 1.4325, DIN X9CrNi18-9, JIS SUS303Se, EN 1.4325, UNS 30302
JIS G4306 Grade SUS302 hot-rolled, solution annealed general
| Property |
Temperature |
Value |
Comment |
| Density |
20.0 °C |
Density of 7.9 - 8.2 g/cm³ |
Typical for Austenitic Stainless Steel |
JIS G4306 Grade SUS302 hot-rolled, solution annealed thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
20.0 °C |
Coefficient of thermal expansion of 1.7E-5 - 1.9E-5 1/K |
Typical for Austenitic Stainless Steel |
| Melting point |
- |
Melting point of 1375 - 1450 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 440 J/(kg·K) |
Typical for Austenitic Stainless Steel |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 11 - 21 W/(m·K) |
Typical for Austenitic Stainless Steel |
JIS G4306 Grade SUS302 hot-rolled, solution annealed chemical
| Property |
Value |
| Carbon |
Carbon of 0.15 % |
| Chromium |
Chromium of 17 - 19 % |
| Iron |
Iron of 67.78 - 75 % |
| Manganese |
Manganese of 2 % |
| Nickel |
Nickel of 8 - 10 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.03 % |
JIS G4306 Grade SUS302 hot-rolled, solution annealed electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
JIS G4306 Grade SUS302 hot-rolled, solution annealed mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 195 GPa |
Typical for Austenitic Stainless Steel |
| Elongation |
20.0 °C |
Elongation of 40 % |
- |
| Poisson's ratio |
20.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 520 MPa |
- |
| Yield strength |
20.0 °C |
Yield strength of 206 MPa |
- |