JIS G4305 Grade SUS302 solution treated
Equivalent material: GOST 12Х18Н9, GOST 12H18N9, AS 302, NF Z10CN18-09, BS 302S25, BS 302S26, BS 302S31, UNI X10CrNi1809, UNE X10CrNi189, SIS 2332-02, AMS 5515, AMS 5516, AMS 5600, AMS 5636, AMS 5637, AMS 5688, AMS 5693, AMS 7210, AMS 7241, AMS 7472, ASME 302, ASTM 302, ASTM MT302, MIL 302, MIL S-5059, MIL S-7720, MIL S-862, AISI 302, SAE 302, UNS S30200, DIN 1.4325, DIN X9CrNi18-9, JIS SUS303Se, EN 1.4325, UNS 30302
JIS G4305 Grade SUS302 solution treated general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.9 - 8.2 g/cm³ |
Typical for Austenitic Stainless Steel |
JIS G4305 Grade SUS302 solution treated thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.7E-5 - 1.9E-5 1/K |
Typical for Austenitic Stainless Steel |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 440 J/(kg·K) |
Typical for Austenitic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 11 - 21 W/(m·K) |
Typical for Austenitic Stainless Steel |
JIS G4305 Grade SUS302 solution treated electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
JIS G4305 Grade SUS302 solution treated mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 195 GPa |
Typical for Austenitic Stainless Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 40 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 187 [-] |
- |
| Hardness, Rockwell B |
23.0 °C |
Hardness, Rockwell B of 90 [-] |
- |
| Hardness, Vickers |
23.0 °C |
Hardness, Vickers of 200 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 520 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 205 MPa |
- |