JIS G4305 Grade SUS410L annealed
Equivalent material: DIN 1.4003, DIN X2Cr11, DIN X2CrNi12, AFNOR X2CrNi12, BS X2CrNi12, AISI S41050, AISI S41003, SAE S41050, SAE S41003, EN X2CrNi12, EN 1.4003, ISO X2CrNi12, ISO 4003-410-77-I, ISO 61, ISO FP12C, GB/T S11213, GB/T 022Cr12Ni, GB/T 00Cr12, GB/T 022Cr12, ASTM S41050, ASTM S40977, ASTM S41003, UNS S40977, UNS S41003, UNS S41050, DIN 1.4030, EN 1.4030, ISO X2C12
JIS G4305 Grade SUS410L annealed general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.6 - 7.8 g/cm³ |
Typical for Ferritic Stainless Steel |
JIS G4305 Grade SUS410L annealed thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 9.3E-6 - 1.2E-5 1/K |
Typical for Ferritic Stainless Steel |
| Melting point |
- |
Melting point of 1425 - 1530 °C |
Typical for Ferritic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 420 - 586 J/(kg·K) |
Typical for Ferritic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 11 - 22 W/(m·K) |
Typical for Ferritic Stainless Steel |
JIS G4305 Grade SUS410L annealed electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 6E-7 - 7.5E-7 Ω·m |
Typical for Ferritic Stainless Steel |
JIS G4305 Grade SUS410L annealed mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 220 GPa |
Typical for Ferritic Stainless Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 22 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 183 [-] |
- |
| Hardness, Rockwell B |
23.0 °C |
Hardness, Rockwell B of 88 [-] |
- |
| Hardness, Vickers |
23.0 °C |
Hardness, Vickers of 200 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Ferritic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Ferritic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 360 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 195 MPa |
- |