JIS G4305 Grade SUS321 solution treated
Equivalent material: AISI 321, SAE 321, ASTM TP321, ASTM 321, UNS S32100, ASTM F321, ASTM Grade 8T, ASTM S32100, ASTM FP321, ASTM MT321, DIN 1.4541, DIN X6CrNiTi18-10, DIN X10CrNiMoTi18-10, AFNOR Z6CNT18-10, BS 321S12, BS 321S51, UNI X6CrNiTi1811, SS 2337, UNE F.3553, UNE F.3523, JIS SUS321TPY, JIS SUS321TP, JIS SUS321TF, JIS SUS321TB, EN X6CrNiTi18-10, EN 1.4541, GOST 06Ch18N10T, GOST 08X18H10T, GOST 12X18H10T, GB 0Cr18Ni11Ti, IS X04Cr18Ni10Ti, DIN 1.4878, DIN X12CrNiTi18-9, DIN X8CrNiTi18-10, AFNOR X8CrNiTi18-10, JIS SUS321HTB, JIS SUS321HTP, JIS SUS321HTF, JIS SUS321TKA, EN X8CrNiTi18-10, EN 1.4878, ASTM Type 321, JIS SUSF321, ASTM Grade F321
JIS G4305 Grade SUS321 solution treated general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.9 - 8.2 g/cm³ |
Typical for Austenitic Stainless Steel |
JIS G4305 Grade SUS321 solution treated thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.7E-5 - 1.9E-5 1/K |
Typical for Austenitic Stainless Steel |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 440 J/(kg·K) |
Typical for Austenitic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 11 - 21 W/(m·K) |
Typical for Austenitic Stainless Steel |
JIS G4305 Grade SUS321 solution treated electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
JIS G4305 Grade SUS321 solution treated mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 195 GPa |
Typical for Austenitic Stainless Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 40 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 187 [-] |
- |
| Hardness, Rockwell B |
23.0 °C |
Hardness, Rockwell B of 90 [-] |
- |
| Hardness, Vickers |
23.0 °C |
Hardness, Vickers of 200 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 520 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 205 MPa |
- |