JIS G4304 Grade SUS434 annealed
Equivalent material: GB/T 1Cr17Mo, GB 1Cr17Mo, DIN X6CrMo171, UNI CB20FF, UNI X8CrMo17, EN X6CrMo17-1, UNE X6CrMo171, ASTM 434, AISI 434, SAE S43400, DIN 1.4113, DIN X6CrMo17, DIN X6CrMo17-1, AFNOR Z8CD17-01, BS 434S17, SS 2325, AISI S43400, SAE 434, EN 1.4113, UNS S43400
JIS G4304 Grade SUS434 annealed general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.6 - 7.8 g/cm³ |
Typical for Ferritic Stainless Steel |
JIS G4304 Grade SUS434 annealed thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 9.3E-6 - 1.2E-5 1/K |
Typical for Ferritic Stainless Steel |
| Melting point |
- |
Melting point of 1425 - 1530 °C |
Typical for Ferritic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 420 - 586 J/(kg·K) |
Typical for Ferritic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 11 - 22 W/(m·K) |
Typical for Ferritic Stainless Steel |
JIS G4304 Grade SUS434 annealed electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 6E-7 - 7.5E-7 Ω·m |
Typical for Ferritic Stainless Steel |
JIS G4304 Grade SUS434 annealed mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 220 GPa |
Typical for Ferritic Stainless Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 22 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 183 [-] |
- |
| Hardness, Rockwell B |
23.0 °C |
Hardness, Rockwell B of 88 [-] |
- |
| Hardness, Vickers |
23.0 °C |
Hardness, Vickers of 200 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Ferritic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Ferritic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 450 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 205 MPa |
- |