DIN 17441 Grade X6CrMo17-1 soft annealed (+A)
DIN 17441 Grade X6CrMo17-1 soft annealed (+A) introduction
Properties:
- 17%-Cr-steel with Mo additives
- high polishable
- higher resistance to media which arise in drive operation (road salt)
- especially developed for automobile industry
Application:
- as hub caps, fender, radiator cowling, window frame
- aprons for headlights, tail light, decorative parts
Equivalent material: AFNOR Z8CD17-01, BS 434S17, ISO 9c, UNI X8CrMo17, JIS SUS434, SS 2325, ASTM 434, DIN 1.4113, DIN X6CrMo17, AISI 434, AISI S43400, SAE 434, SAE S43400, EN X6CrMo17-1, EN 1.4113, UNS S43400
DIN 17441 Grade X6CrMo17-1 soft annealed (+A) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.56 - 7.7 g/cm³ |
DIN 17441 Grade X6CrMo17-1 soft annealed (+A) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
20.0 °C |
Coefficient of thermal expansion of 9.9E-6 1/K |
- |
| - |
100.0 °C |
Coefficient of thermal expansion of 1E-5 - 1.03E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.05E-5 - 1.08E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.05E-5 - 1.12E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.05E-5 - 1.16E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.1E-5 - 1.19E-5 1/K |
- |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.21E-5 1/K |
- |
| - |
700.0 °C |
Coefficient of thermal expansion of 1.24E-5 1/K |
- |
| - |
800.0 °C |
Coefficient of thermal expansion of 1.29E-5 1/K |
- |
| Melting point |
- |
Melting point of 1425 - 1530 °C |
Typical for Ferritic Stainless Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 450 - 460 J/(kg·K) |
- |
| - |
100.0 °C |
Specific heat capacity of 482 J/(kg·K) |
- |
| - |
200.0 °C |
Specific heat capacity of 506 J/(kg·K) |
- |
| - |
300.0 °C |
Specific heat capacity of 525 J/(kg·K) |
- |
| - |
400.0 °C |
Specific heat capacity of 547 J/(kg·K) |
- |
| - |
500.0 °C |
Specific heat capacity of 576 J/(kg·K) |
- |
| - |
600.0 °C |
Specific heat capacity of 616 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 16 - 25 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 17.2 W/(m·K) |
- |
| - |
200.0 °C |
Thermal conductivity of 18.6 W/(m·K) |
- |
| - |
300.0 °C |
Thermal conductivity of 20 W/(m·K) |
- |
| - |
400.0 °C |
Thermal conductivity of 21.2 W/(m·K) |
- |
| - |
500.0 °C |
Thermal conductivity of 22.3 W/(m·K) |
- |
| - |
600.0 °C |
Thermal conductivity of 23.3 W/(m·K) |
- |
| - |
700.0 °C |
Thermal conductivity of 24.1 W/(m·K) |
- |
| - |
800.0 °C |
Thermal conductivity of 25.5 W/(m·K) |
- |
| - |
900.0 °C |
Thermal conductivity of 26.9 W/(m·K) |
- |
| - |
1000.0 °C |
Thermal conductivity of 28.3 W/(m·K) |
- |
| Thermal diffusivity |
20.0 °C |
Thermal diffusivity of 4.7 mm²/s |
- |
| - |
100.0 °C |
Thermal diffusivity of 4.5 mm²/s |
- |
| - |
200.0 °C |
Thermal diffusivity of 4.5 mm²/s |
- |
| - |
300.0 °C |
Thermal diffusivity of 4.6 mm²/s |
- |
| - |
400.0 °C |
Thermal diffusivity of 4.4 mm²/s |
- |
| - |
500.0 °C |
Thermal diffusivity of 4.1 mm²/s |
- |
| - |
600.0 °C |
Thermal diffusivity of 3.6 mm²/s |
- |
DIN 17441 Grade X6CrMo17-1 soft annealed (+A) chemical
| Property |
Value |
| Carbon |
Carbon of 0.08 % |
| Chromium |
Chromium of 16 - 18 % |
| Manganese |
Manganese of 0.9 - 1.3 % |
| Molybdenum |
Molybdenum of 0.9 - 1.3 % |
| Phosphorus |
Phosphorus of 0.05 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.03 % |
DIN 17441 Grade X6CrMo17-1 soft annealed (+A) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 7E-7 - 9.06E-7 Ω·m |
| - |
100.0 °C |
Electrical resistivity of 9.42E-7 Ω·m |
| - |
200.0 °C |
Electrical resistivity of 9.87E-7 Ω·m |
| - |
300.0 °C |
Electrical resistivity of 1.03E-6 Ω·m |
| - |
400.0 °C |
Electrical resistivity of 1.08E-6 Ω·m |
| - |
500.0 °C |
Electrical resistivity of 1.12E-6 Ω·m |
| - |
600.0 °C |
Electrical resistivity of 1.18E-6 Ω·m |
| - |
700.0 °C |
Electrical resistivity of 1.22E-6 Ω·m |
| - |
800.0 °C |
Electrical resistivity of 1.24E-6 Ω·m |
| - |
900.0 °C |
Electrical resistivity of 1.26E-6 Ω·m |
| - |
1000.0 °C |
Electrical resistivity of 1.27E-6 Ω·m |
DIN 17441 Grade X6CrMo17-1 soft annealed (+A) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 216 - 218 GPa |
- |
| - |
100.0 °C |
Elastic modulus of 213 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 206 - 207 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 198 - 200 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 190 - 192 GPa |
- |
| - |
500.0 °C |
Elastic modulus of 180 GPa |
- |
| - |
600.0 °C |
Elastic modulus of 167 GPa |
- |
| - |
700.0 °C |
Elastic modulus of 150 GPa |
- |
| Elongation |
20.0 °C |
Elongation of 20 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Ferritic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Ferritic Stainless Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 480 - 630 MPa |
- |
| Yield strength Rp0.2 |
20.0 °C |
Yield strength Rp0.2 of 260 MPa |
- |