JIS G4304 Grade SUS316LN solution treated
Equivalent material: GB/T 00Cr17Ni13Mo2N, GB/T ZG10Cr13, GB 00Cr17Ni13Mo2N, DIN X2CrNiMoN17133, DIN X2CrNiMoN17122, EN X2CrNiMoN17-11-2, NF Z2CND17-12Az, NF Z2CND17-13Az, NF Z3CND17-11Az, NF Z3CND17-12Az, BS 316S61, BS 316S63, UNI X2CrNiMoN1712, UNI X2CrNiMoN1713, ÖNORM X2CrNiMoN17122KKW, ÖNORM X2CrNiMoN17133KKW, UNE X8CrNiMo27-05, UNE X2CrNiMoN17122, UNE X2CrNiMoN17133, SIS 2375, ASTM TP316LN, ASTM 316LN, ASTM B8MLN, ASTM B8MLNA, ASTM CR316LN, ASTM WP316LN, ASTM 18Cr 8Ni Mod. with Mo, Ni, ASTM F316LN, ASTM 8MLN, ASTM 8MLNA, AISI 316LN, SAE 316LN, EN X2CrNiMoN17-13-3, DIN 1.4406, DIN X2CrNiMoN17-11-2, AFNOR Z3CND17-11Az, BS 316S13, UNE F.3542, EN 1.4406, UNS S31653, ASTM Grade 8MLN, DIN 1.4429, DIN X2CrNiMoN17-13-3, AFNOR Z7CND18-12-03, SS 2375, JIS SUSF316LN, EN 1.4429, ASTM S31654, UNS S31654
JIS G4304 Grade SUS316LN solution treated general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.9 - 8.2 g/cm³ |
Typical for Austenitic Stainless Steel |
JIS G4304 Grade SUS316LN solution treated thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.7E-5 - 1.9E-5 1/K |
Typical for Austenitic Stainless Steel |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 440 J/(kg·K) |
Typical for Austenitic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 11 - 21 W/(m·K) |
Typical for Austenitic Stainless Steel |
JIS G4304 Grade SUS316LN solution treated electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
JIS G4304 Grade SUS316LN solution treated mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 195 GPa |
Typical for Austenitic Stainless Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 40 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 217 [-] |
- |
| Hardness, Rockwell B |
23.0 °C |
Hardness, Rockwell B of 95 [-] |
- |
| Hardness, Vickers |
23.0 °C |
Hardness, Vickers of 220 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 550 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 245 MPa |
- |