EN 10088-1 Grade X2CrNiMoN17-13-3 solution annealed (+AT)
EN 10088-1 Grade X2CrNiMoN17-13-3 solution annealed (+AT) introduction
Material X2CrNiMoN17-13-3 is comparable to X 2 CrNiMoN 17 13 3 acc. to DIN17440 : 1985-07. It is a fully austenitic steel that is suitable for mirror finishing. It shows higher strength owing to nitrogen alloying and owing to more molybdenum addition higher corrosion resistance especially to non oxidizing acids and halogenated media than 1.4406. Resistance to intercrystalline corrosion in delivery condition as well as in sensitized condition. The material shows higher resistance to selective corrosion than 1.4435 and excellent limiting fatigue stres behavior also under chemical load. Furthermore it shows good cryogenic toughness. It is therefore suitable for refrigeration up to -270 °C.
Equivalent material: GB 00Cr17Ni13Mo2N, SFS 753, SFS X2CrNiMoN17-11-3, AFNOR Z2CND17-13Az, BS 316S63, GB S31653, ISO X2CrNiMoN17-12-3, ISO X2CrNiMoN17-13-3E, ISO X2CrNiMoN17-13-3, ISO X2CrNiMoN17-13, UNI X2CrNiMo17-13, JIS SUSF316LN, JIS SUS316LN, ÖNORM X2CrNiMoN17-13-3KKW, KS STS316LN, KS STSF316LN, SS 2375, UNS S31653, ASTM TP316LN, ASTM 316LN, ASTM F316LN, ASTM B8MLN, ASTM B8MLNA, ASTM 8MLN, ASTM 8MLNA, ASTM WP316LN, ASTM S31653, SAE 316LN, GB 022Cr17Ni12Mo2N, ISO 4429-316-53-I, ISO AM32B, ASTM A240Type316LN, ASTM A276Type316LN, ASTM A480Type316LN, ASTM A959UNSS31653, AISI Type316LN, DIN 1.4429, DIN X2CrNiMoN17-13-3, AFNOR Z7CND18-12-03, UNI X2CrNiMoN1713, AISI 316LN, EN 1.4429, ASTM S31654, UNS S31654
EN 10088-1 Grade X2CrNiMoN17-13-3 solution annealed (+AT) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 8 - 8.01 g/cm³ |
EN 10088-1 Grade X2CrNiMoN17-13-3 solution annealed (+AT) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
-100.0 °C |
Coefficient of thermal expansion of 1.49E-5 1/K |
- |
| - |
20.0 °C |
Coefficient of thermal expansion of 1.61E-5 1/K |
- |
| - |
100.0 °C |
Coefficient of thermal expansion of 1.6E-5 - 1.67E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.65E-5 - 1.72E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.7E-5 - 1.77E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.75E-5 - 1.81E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.8E-5 - 1.84E-5 1/K |
- |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.88E-5 1/K |
- |
| - |
700.0 °C |
Coefficient of thermal expansion of 1.91E-5 1/K |
- |
| - |
800.0 °C |
Coefficient of thermal expansion of 1.94E-5 1/K |
- |
| - |
900.0 °C |
Coefficient of thermal expansion of 1.97E-5 1/K |
- |
| - |
1000.0 °C |
Coefficient of thermal expansion of 2E-5 1/K |
- |
| Max service temperature, long |
- |
Max service temperature, long of -270 - 0 °C |
- |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
-100.0 °C |
Specific heat capacity of 440 J/(kg·K) |
- |
| - |
20.0 °C |
Specific heat capacity of 472 - 500 J/(kg·K) |
- |
| - |
100.0 °C |
Specific heat capacity of 487 J/(kg·K) |
- |
| - |
200.0 °C |
Specific heat capacity of 503 J/(kg·K) |
- |
| - |
300.0 °C |
Specific heat capacity of 512 J/(kg·K) |
- |
| - |
400.0 °C |
Specific heat capacity of 520 J/(kg·K) |
- |
| - |
500.0 °C |
Specific heat capacity of 530 J/(kg·K) |
- |
| - |
600.0 °C |
Specific heat capacity of 541 J/(kg·K) |
- |
| - |
700.0 °C |
Specific heat capacity of 551 J/(kg·K) |
- |
| - |
800.0 °C |
Specific heat capacity of 559 J/(kg·K) |
- |
| - |
900.0 °C |
Specific heat capacity of 565 J/(kg·K) |
- |
| - |
1000.0 °C |
Specific heat capacity of 571 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 13.5 - 15 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 14.9 W/(m·K) |
- |
| - |
200.0 °C |
Thermal conductivity of 16.7 W/(m·K) |
- |
| - |
300.0 °C |
Thermal conductivity of 18.3 W/(m·K) |
- |
| - |
400.0 °C |
Thermal conductivity of 19.8 W/(m·K) |
- |
| - |
500.0 °C |
Thermal conductivity of 21.3 W/(m·K) |
- |
| - |
600.0 °C |
Thermal conductivity of 22.7 W/(m·K) |
- |
| - |
700.0 °C |
Thermal conductivity of 24.2 W/(m·K) |
- |
| - |
800.0 °C |
Thermal conductivity of 25.6 W/(m·K) |
- |
| Thermal diffusivity |
20.0 °C |
Thermal diffusivity of 3.6 mm²/s |
- |
| - |
100.0 °C |
Thermal diffusivity of 3.7 mm²/s |
- |
| - |
200.0 °C |
Thermal diffusivity of 4 mm²/s |
- |
| - |
300.0 °C |
Thermal diffusivity of 4.4 mm²/s |
- |
| - |
400.0 °C |
Thermal diffusivity of 4.6 mm²/s |
- |
| - |
500.0 °C |
Thermal diffusivity of 4.7 mm²/s |
- |
| - |
600.0 °C |
Thermal diffusivity of 4.9 mm²/s |
- |
| - |
700.0 °C |
Thermal diffusivity of 5.2 mm²/s |
- |
| - |
800.0 °C |
Thermal diffusivity of 5.5 mm²/s |
- |
EN 10088-1 Grade X2CrNiMoN17-13-3 solution annealed (+AT) chemical
| Property |
Value |
| Carbon |
Carbon of 0.03 % |
| Chromium |
Chromium of 16.5 - 18.5 % |
| Manganese |
Manganese of 2 % |
| Molybdenum |
Molybdenum of 2.5 - 3 % |
| Nickel |
Nickel of 11 - 14 % |
| Nitrogen |
Nitrogen of 0.12 - 0.22 % |
| Phosphorus |
Phosphorus of 0.05 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.015 % |
EN 10088-1 Grade X2CrNiMoN17-13-3 solution annealed (+AT) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 7.5E-7 - 7.75E-7 Ω·m |
| - |
100.0 °C |
Electrical resistivity of 8.42E-7 Ω·m |
| - |
200.0 °C |
Electrical resistivity of 9.04E-7 Ω·m |
| - |
300.0 °C |
Electrical resistivity of 9.62E-7 Ω·m |
| - |
400.0 °C |
Electrical resistivity of 1.01E-6 Ω·m |
| - |
500.0 °C |
Electrical resistivity of 1.06E-6 Ω·m |
| - |
600.0 °C |
Electrical resistivity of 1.1E-6 Ω·m |
| - |
700.0 °C |
Electrical resistivity of 1.13E-6 Ω·m |
| - |
800.0 °C |
Electrical resistivity of 1.16E-6 Ω·m |
EN 10088-1 Grade X2CrNiMoN17-13-3 solution annealed (+AT) mechanical
| Property |
Temperature |
Value |
| Elastic modulus |
-100.0 °C |
Elastic modulus of 206 GPa |
| - |
20.0 °C |
Elastic modulus of 196 - 200 GPa |
| - |
100.0 °C |
Elastic modulus of 190 - 194 GPa |
| - |
200.0 °C |
Elastic modulus of 182 - 186 GPa |
| - |
300.0 °C |
Elastic modulus of 174 - 179 GPa |
| - |
400.0 °C |
Elastic modulus of 166 - 172 GPa |
| - |
500.0 °C |
Elastic modulus of 158 - 165 GPa |
| - |
600.0 °C |
Elastic modulus of 150 GPa |
| - |
700.0 °C |
Elastic modulus of 142 GPa |
| - |
800.0 °C |
Elastic modulus of 134 GPa |
| Elongation |
20.0 °C |
Elongation of 40 % |
| Elongation A80, transverse |
20.0 °C |
Elongation A80, transverse of 35 - 40 % |
| Elongation, transverse |
20.0 °C |
Elongation, transverse of 30 - 40 % |
| Hardness, Brinell |
20.0 °C |
Hardness, Brinell of 250 [-] |
| Hardness, Brinell, trans |
20.0 °C |
Hardness, Brinell, trans of 250 [-] |
| Poisson's ratio |
20.0 °C |
Poisson's ratio of 0.28 [-] |
| Shear modulus |
20.0 °C |
Shear modulus of 77.3 GPa |
| Tensile strength |
20.0 °C |
Tensile strength of 580 - 800 MPa |
| Tensile strength, transverse |
20.0 °C |
Tensile strength, transverse of 580 - 800 MPa |
| Yield strength Rp0.2 |
20.0 °C |
Yield strength Rp0.2 of 200 - 280 MPa |
| - |
100.0 °C |
Yield strength Rp0.2 of 211 - 215 MPa |
| - |
150.0 °C |
Yield strength Rp0.2 of 185 - 195 MPa |
| - |
200.0 °C |
Yield strength Rp0.2 of 167 - 175 MPa |
| - |
250.0 °C |
Yield strength Rp0.2 of 155 - 180 MPa |
| - |
300.0 °C |
Yield strength Rp0.2 of 145 - 170 MPa |
| - |
350.0 °C |
Yield strength Rp0.2 of 140 - 150 MPa |
| - |
400.0 °C |
Yield strength Rp0.2 of 135 - 145 MPa |
| - |
450.0 °C |
Yield strength Rp0.2 of 131 - 140 MPa |
| - |
500.0 °C |
Yield strength Rp0.2 of 129 - 138 MPa |
| - |
550.0 °C |
Yield strength Rp0.2 of 127 - 136 MPa |
| Yield strength Rp0.2, transverse |
20.0 °C |
Yield strength Rp0.2, transverse of 200 - 300 MPa |
| Yield strength Rp1.0 |
20.0 °C |
Yield strength Rp1.0 of 315 MPa |
| - |
100.0 °C |
Yield strength Rp1.0 of 245 - 246 MPa |
| - |
150.0 °C |
Yield strength Rp1.0 of 218 - 225 MPa |
| - |
200.0 °C |
Yield strength Rp1.0 of 198 - 205 MPa |
| - |
250.0 °C |
Yield strength Rp1.0 of 183 - 215 MPa |
| - |
300.0 °C |
Yield strength Rp1.0 of 175 - 205 MPa |
| - |
350.0 °C |
Yield strength Rp1.0 of 169 - 180 MPa |
| - |
400.0 °C |
Yield strength Rp1.0 of 164 - 175 MPa |
| - |
450.0 °C |
Yield strength Rp1.0 of 160 - 170 MPa |
| - |
500.0 °C |
Yield strength Rp1.0 of 158 - 168 MPa |
| - |
550.0 °C |
Yield strength Rp1.0 of 157 - 166 MPa |
| Yield strength Rp1.0, transverse |
20.0 °C |
Yield strength Rp1.0, transverse of 315 - 330 MPa |
Our steel seamlessly integrates into your projects, ensuring flawless and impressive outcomes.
-- Our promise