JIS G4303 Grade SUS410J1 quenched and tempered
Equivalent material: GB/T 1Cr13, GB/T ML1Cr13, GB/T 1Cr13-Q, GB 1Cr13, GB H1Cr13, DIN X15Cr13, NF Z12C13M, NF Z13C13, NF Z15C13, BS 420S29, UNE X15Cr13, MIL 420, GB H0Cr14, GB 0Cr13, GOST 08Х13, GOST 08H13, GOST 08H13-Sh, AS 410S, DIN X6Cr13, NF Z6C13, NF Z8C12, NF Z8C13FF, BS 403S17, BS S.3S61, IS 04Cr13, IS 6527, UNI X6Cr13, EN X6Cr13, UNE AM-X12Cr13, UNE X6Cr13, SIS 2301-02, SIS 2301-22, SIS 2301-23, SIS 2301, AMS 5611, AMS 5612, ASME 410S, ASTM 410S, ASTM 403, ASTM MT403, MIL 403, JIS SUS410S, JIS SUS403, JIS SUS429, AISI 403, AISI 410S, ASTM S41008, SAE 410S, GB/T 0Cr13, ASME 429, ASTM F429, ASTM TP429, ASTM MT429, ASTM WP429, ASTM 429, MIL 429, DIN 1.4024, AISI 410, AISI S41000, SAE 410, SAE S41000, JIS SUS410J1FB, JIS SUS410TB, JIS SUSF410B, JIS SUSF410C, JIS SUSF410A, JIS SUSF410D, EN X15Cr13, EN 1.4024, ISO X15Cr13, ASTM MT410, ASTM 410, ASTM S41000, UNS S41000
JIS G4303 Grade SUS410J1 quenched and tempered general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.6 - 7.7 g/cm³ |
Typical for Martensitic Stainless Steel |
JIS G4303 Grade SUS410J1 quenched and tempered thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1E-5 - 1.5E-5 1/K |
Typical for Martensitic Stainless Steel |
| Melting point |
- |
Melting point of 1370 - 1530 °C |
Typical for Martensitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 460 J/(kg·K) |
Typical for Martensitic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 14 - 31 W/(m·K) |
Typical for Martensitic Stainless Steel |
JIS G4303 Grade SUS410J1 quenched and tempered electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 6E-7 Ω·m |
Typical for Martensitic Stainless Steel |
JIS G4303 Grade SUS410J1 quenched and tempered mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 220 GPa |
Typical for Martensitic Stainless Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 20 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 192 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Martensitic Stainless Steel |
| Reduction of area |
23.0 °C |
Reduction of area of 60 % |
- |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Martensitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 690 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 490 MPa |
- |