JIS G4303 Grade SUS305 solution treated
Equivalent material: GOST 06Х18Н11, DIN X5CrNi1812, NF Z8CN18-12, NF X8CN18-12, NF Z5CN18-11FF, BS 305S17, BS 305S19, UNI X8CrNi1910, UNI X7CrNi1810, ÖNORM X5CrNi1812KKW, EN X4CrNi18-12, UNE X8CrNi1812, AMS 5514, AMS 5685, AMS 5686, ASME 305, ASTM 305, ASTM B8P, ASTM B8PA, ASTM 8P, ASTM TP305, ASTM MT305, ASTM 8PA, JIS SUS305J1, AISI 305, SAE 305, ASTM 308, AISI 308, DIN 1.4303, DIN X5CrNi18-12, DIN X4CrNi18-12, AFNOR Z1CN18-12, AFNOR Z5CN18-11FF, SAE 308, JIS SUSY308, EN 1.4303, GOST 06Ch18N11, GOST 06X18H11, GB 1Cr18Ni12, ASTM ER308, UNS S30500, UNS S30880
JIS G4303 Grade SUS305 solution treated general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.9 - 8.2 g/cm³ |
Typical for Austenitic Stainless Steel |
JIS G4303 Grade SUS305 solution treated thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.7E-5 - 1.9E-5 1/K |
Typical for Austenitic Stainless Steel |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 440 J/(kg·K) |
Typical for Austenitic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 11 - 21 W/(m·K) |
Typical for Austenitic Stainless Steel |
JIS G4303 Grade SUS305 solution treated electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
JIS G4303 Grade SUS305 solution treated mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 195 GPa |
Typical for Austenitic Stainless Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 40 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 187 [-] |
- |
| Hardness, Rockwell B |
23.0 °C |
Hardness, Rockwell B of 90 [-] |
- |
| Hardness, Vickers |
23.0 °C |
Hardness, Vickers of 200 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Reduction of area |
23.0 °C |
Reduction of area of 60 % |
- |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 480 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 175 MPa |
- |