JIS G4051 Grade S58C
Equivalent material: GOST 2, GOST 60G, GOST 60, AS K1060, EN C60, EN C60E, DIN C60, NF CC55, NF XC60, NF C60, BS 60HS, BS 60CS, IS SW, IS C60, UNI C60, UNI 3CD60, UNI C61, UNI 1C60, AMS 7240, ASTM 1060, MIL 5, MIL 7, MIL C6, MIL S-16974, JIS S60CM, AISI 1060, SAE 1060, GB 60, DIN Ck60, GB/T 60, GB/T 60, DIN 1.0601, AFNOR CC55, AFNOR C60, BS 080A62, BS En9, BS 070M55, BS C60, BS 060A62, JIS S60C, JIS SWRH62B, JIS S65C, EN 1.0601, ISO C60, ISO CS60, GB/T CRB970, GB/T U20602, UNS G10600, DIN 1.1221, DIN C60E, AFNOR XC60, AFNOR C60RR, AFNOR 9160C031, AFNOR 9160/C25, AFNOR XC65, AFNOR C60E, BS 070M60, BS CS60, BS C60E, SS 1678, 1064, JIS S65CM, JIS S60C-CSP, JIS S65C-CSP, JIS 30A, JIS 37A, EN C60S, EN 1.1221, ISO C60E, ISO C60E4, ISO S58C, GOST 60GA, GB U20602, UNS G10640
JIS G4051 Grade S58C general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for High Carbon Steel |
JIS G4051 Grade S58C thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 1/K |
Typical for High Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1289 - 1478 °C |
Typical for High Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 486 J/(kg·K) |
Typical for High Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 36 W/(m·K) |
Typical for High Carbon Steel |
JIS G4051 Grade S58C chemical
| Property |
Value |
| Carbon |
Carbon of 0.55 - 0.61 % |
| Iron |
Iron of 98.07 - 98.7 % |
| Manganese |
Manganese of 0.6 - 0.9 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.15 - 0.35 % |
| Sulfur |
Sulfur of 0.035 % |
JIS G4051 Grade S58C electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
JIS G4051 Grade S58C mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for High Carbon Steel |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for High Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 81 GPa |
Typical for High Carbon Steel |