JIS G4051 Grade S25C
Equivalent material: GB 25, GB 1025, GB 25Z, GOST Ст4пс, GOST 25, GOST 25ps, GOST S345K, GOST St4ps, GOST VSt4ps, GOST БСт4пс, GOST ВСт4пс, GOST 25L, AS S1025, AS CS1025, EN C25, EN C26D, EN C25E, DIN D25-2, BS 070M26, IS C25, UNI 1CD25, UNI C25, UNI 3CD25, UNI 1C25, ÖNORM RC25, AMS 5077, ASTM 1025, ASTM M1025, MIL 1025, MIL CS1025, MIL S-7952A, MIL T-5066, JIS S28C, AISI 1025, AISI M1025, SAE 1025, GB/T 25, GB/T 25, GB/T ML25, DIN 1.1158, DIN Ck25, DIN C25E, AFNOR XC25, AFNOR C25E, BS C25E, EN 1.1158, ISO C25E4, ISO C25E, ISO S25C, GB/T U20252, GB/T ML25, GB/T U40252, ASTM Grade 1025, UNS G10250
JIS G4051 Grade S25C general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
JIS G4051 Grade S25C thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
JIS G4051 Grade S25C chemical
| Property |
Value |
| Carbon |
Carbon of 0.22 - 0.28 % |
| Iron |
Iron of 98.7 - 99.33 % |
| Manganese |
Manganese of 0.3 - 0.6 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 0.15 - 0.35 % |
| Sulfur |
Sulfur of 0.035 % |
JIS G4051 Grade S25C magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
JIS G4051 Grade S25C electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
JIS G4051 Grade S25C mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |