JIS G3463 Grade SUS410TB
Equivalent material: GB 1Cr12, GB 1Cr13, GOST 12Х13, GOST 12H13, GOST 12H13-Sh, GOST 15H13L, AS 410, AS En56A, DIN X10Cr13, NF Z12C13, NF Z10C13, BS 410S21, BS 410S21-690, BS 410S21-720, BS 410S21-760, BS 410S21-750, BS 410S21-770, BS 410C21, IS 12Cr13, UNI X12Cr13, UNI X10Cr13, UNI X12Cr13KG, UNI X12Cr13KW, EN X12Cr13, UNE X10Cr13, SIS 2302-03, SIS 2302, AMS 5504, AMS 5505, AMS 5591, AMS 5613, AMS 5776, AMS 5821, AMS 7493, ASME 6, ASME 410, ASTM TP410, ASTM 410, ASTM F6, ASTM 13Cr, ASTM F6a-1, ASTM 6, ASTM B6, ASTM F6a-2, ASTM F6a-3, ASTM F6a-4, ASTM B6X, ASTM MT410, MIL 410, JIS SUS410TKA, JIS SUS410, AISI 410, SAE 410, SAE 51410, GB/T 1Cr12, DIN 1.4024, DIN X15Cr13, AISI S41000, SAE S41000, JIS SUS410J1FB, JIS SUS410J1, JIS SUSF410B, JIS SUSF410C, JIS SUSF410A, JIS SUSF410D, EN X15Cr13, EN 1.4024, ISO X15Cr13, ASTM S41000, UNS S41000
JIS G3463 Grade SUS410TB general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.6 - 7.7 g/cm³ |
Typical for Martensitic Stainless Steel |
JIS G3463 Grade SUS410TB thermal
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 220 GPa |
Typical for Martensitic Stainless Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 11 - 20 % |
- |
| Hardness, Rockwell B |
23.0 °C |
Hardness, Rockwell B of 95 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Martensitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Martensitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 410 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 205 MPa |
- |
JIS G3463 Grade SUS410TB magnetic
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 6E-7 Ω·m |
Typical for Martensitic Stainless Steel |
JIS G3463 Grade SUS410TB electrical
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1E-5 - 1.5E-5 1/K |
Typical for Martensitic Stainless Steel |
| Melting point |
- |
Melting point of 1370 - 1530 °C |
Typical for Martensitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 460 J/(kg·K) |
Typical for Martensitic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 14 - 31 W/(m·K) |
Typical for Martensitic Stainless Steel |
JIS G3463 Grade SUS410TB mechanical
| Property |
Value |
| Wall thickness |
Wall thickness of 1 - 8 mm |