JIS G3317 Grade SZAC570 cold-rolled

JIS G3317 Grade SZAC570 cold-rolled

Equivalent material: DIN 1.0531, DIN FeE550G, DIN St50, DIN S550GD, AFNOR S550GD, BS S550GD, JIS SGMC570, JIS SGC570, JIS SZAH540, JIS SGLC570, JIS SGLH540, EN S550GD, EN 1.0531, ISO 550, GB/T S550GD, ASTM SS Grade 550

JIS G3317 Grade SZAC570 cold-rolled general

Property Temperature Value Comment
Density 23.0 °C Density of 7.8 - 7.9 g/cm³ Typical for Low Carbon Steel

JIS G3317 Grade SZAC570 cold-rolled thermal

Property Temperature Value Comment
Coefficient of thermal expansion 23.0 °C Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K Typical for Low Carbon Steel
Max service temperature - Max service temperature of 500 °C Typical for Carbon Steel
Melting point - Melting point of 1480 - 1526 °C Typical for Low Carbon Steel
Specific heat capacity 23.0 °C Specific heat capacity of 465 J/(kg·K) Typical for Low Carbon Steel
Thermal conductivity 23.0 °C Thermal conductivity of 25 - 93 W/(m·K) Typical for Low Carbon Steel

JIS G3317 Grade SZAC570 cold-rolled magnetic

Property Value Comment
Curie temperature Curie temperature of 770 °C Typical for Low Carbon Steel

JIS G3317 Grade SZAC570 cold-rolled electrical

Property Temperature Value Comment
Electrical resistivity 23.0 °C Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m Typical for Carbon Steel

JIS G3317 Grade SZAC570 cold-rolled mechanical

Property Temperature Value Comment
Elastic modulus 23.0 °C Elastic modulus of 200 - 215 GPa Typical for Low Carbon Steel
Poisson's ratio 23.0 °C Poisson's ratio of 0.29 [-] Typical for Low Carbon Steel
Shear modulus 23.0 °C Shear modulus of 82 GPa Typical for Low Carbon Steel
Tensile strength 23.0 °C Tensile strength of 570 MPa -
Yield strength 23.0 °C Yield strength of 560 MPa -