JIS G3214 Grade SUSF310
Equivalent material: GB/T 1Cr25Ni20Si2, GB/T 2Cr25Ni20, GB 2Cr25Ni20, GOST Ch25N20L, AS 2837, AS 310, DIN X15CrNiSi2520, NF Z12CN25-20, BS 310S24, BS 310S31, UNI X22CrNi2520, UNI X16CrNiSi2520, EN X15CrNiSi25-21, UNE X15CrNiSi25-20, SIS 2361-02, SIS 2376, ASME 310, ASTM 310, ASTM F310, ASTM TP310, MIL 310, JIS SUS310STB, JIS SUS310STP, JIS SUH310, JIS SUSY310, AISI 310, GOST 20H25N19S2L, AMS 5652, AMS 5522, AMS 7490, ASTM 314, AISI 314, ASTM S31500, AISI S31500, UNS S31000
JIS G3214 Grade SUSF310 general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.9 - 8.2 g/cm³ |
Typical for Austenitic Stainless Steel |
JIS G3214 Grade SUSF310 thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.7E-5 - 1.9E-5 1/K |
Typical for Austenitic Stainless Steel |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 440 J/(kg·K) |
Typical for Austenitic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 11 - 21 W/(m·K) |
Typical for Austenitic Stainless Steel |
JIS G3214 Grade SUSF310 electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
JIS G3214 Grade SUSF310 mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 195 GPa |
Typical for Austenitic Stainless Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 29 - 34 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 187 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Reduction of area |
23.0 °C |
Reduction of area of 40 - 50 % |
- |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 480 - 520 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 205 MPa |
- |