JIS G3118 Grade SGV450
Equivalent material: JIS SGV410, JIS SGV480, DIN 1.0425, DIN St 45-8, DIN St 42-8, DIN H II, DIN P265GH, AFNOR A42AP, AFNOR A42CP, AFNOR P265GH, BS 151-400, BS 161-400, BS 164-400, BS P265GH, UNI Fe410-1KW, UNI Fe410KG, UNI Fe410KT, UNI P265GH, UNE A42RCI, JIS SG295, EN P265GH, EN 1.0425, ISO F9, ISO PH26, ISO P265GH, GOST 16K, GOST 20K, UNS K02704, UNS K02505, UNS K02801, DIN 1.0473, DIN 19Mn6, DIN P355GH, AFNOR P355GH, AFNOR A52CP, BS P355GH, BS 224-490, JIS SPV36, JIS SPV355, EN P355GH, EN 1.0473, ISO P355GH, ISO P520Q, ISO P550Q, ISO PH29, GB/T Q345R, GB/T L13454, ASTM Grade A, UNS K12437, DIN 1.0481, DIN 17Mn4, DIN P295GH, AFNOR A48CP, AFNOR P295GH, BS 224-460B, BS P295GH, JIS SG365, JIS SPV315, JIS STB510, EN P295GH, EN 1.0481, ISO P295GH, ISO PT490, ASTM Grade C, UNS K03501, UNS K03102, UNS K03101, UNS K02203
JIS G3118 Grade SGV450 general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
JIS G3118 Grade SGV450 thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
JIS G3118 Grade SGV450 magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
JIS G3118 Grade SGV450 electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
JIS G3118 Grade SGV450 mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Elongation A5 |
23.0 °C |
Elongation A5 of 19 - 23 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 450 - 540 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 245 MPa |
- |