ISO 4957 Grade X36CrMo17 quenched and tempered (+QT)
ISO 4957 Grade X36CrMo17 quenched and tempered (+QT) introduction
for tools for machining of chemcial aggressive thermoplastics
Equivalent material: ISO 38CrMo15, DIN X38CrMo16, DIN 1.2316, AFNOR X38CrMo16, AFNOR X38CrMo16-1, AFNOR Z38CD16-01, BS X38CrMo16, AISI 420mod, SAE 420mod, EN X38CrMo16, EN X38CrMo161, EN 1.2316, ISO X38CrMo16
ISO 4957 Grade X36CrMo17 quenched and tempered (+QT) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.65 g/cm³ |
ISO 4957 Grade X36CrMo17 quenched and tempered (+QT) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
-100.0 °C |
Coefficient of thermal expansion of 9.2E-6 1/K |
- |
| - |
20.0 °C |
Coefficient of thermal expansion of 9.9E-6 1/K |
- |
| - |
100.0 °C |
Coefficient of thermal expansion of 1.03E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.08E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.12E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.16E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.19E-5 1/K |
- |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.21E-5 1/K |
- |
| - |
700.0 °C |
Coefficient of thermal expansion of 1.24E-5 1/K |
- |
| - |
800.0 °C |
Coefficient of thermal expansion of 1.29E-5 1/K |
- |
| - |
900.0 °C |
Coefficient of thermal expansion of 1.34E-5 1/K |
- |
| - |
1000.0 °C |
Coefficient of thermal expansion of 1.39E-5 1/K |
- |
| Melting point |
- |
Melting point of 1370 - 1425 °C |
Typical for Tool And Machining Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 450 J/(kg·K) |
- |
| - |
100.0 °C |
Specific heat capacity of 482 J/(kg·K) |
- |
| - |
200.0 °C |
Specific heat capacity of 506 J/(kg·K) |
- |
| - |
300.0 °C |
Specific heat capacity of 525 J/(kg·K) |
- |
| - |
400.0 °C |
Specific heat capacity of 547 J/(kg·K) |
- |
| - |
500.0 °C |
Specific heat capacity of 576 J/(kg·K) |
- |
| - |
600.0 °C |
Specific heat capacity of 616 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 19.6 W/(m·K) |
- |
| Thermal diffusivity |
20.0 °C |
Thermal diffusivity of 5.7 mm²/s |
- |
ISO 4957 Grade X36CrMo17 quenched and tempered (+QT) chemical
| Property |
Value |
| Carbon |
Carbon of 0.33 - 0.43 % |
| Chromium |
Chromium of 15 - 17 % |
| Manganese |
Manganese of 1 % |
| Molybdenum |
Molybdenum of 1 - 1.3 % |
| Nickel |
Nickel of 1 % |
| Phosphorus |
Phosphorus of 0.03 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.03 % |
ISO 4957 Grade X36CrMo17 quenched and tempered (+QT) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 6.17E-7 Ω·m |
ISO 4957 Grade X36CrMo17 quenched and tempered (+QT) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 196 GPa |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Tool And Machining Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 79 GPa |
Typical for Tool And Machining Steel |