IS 6603 Grade 15Cr16Ni2
Equivalent material: DIN 1.4057, DIN X17CrNi16-2, AFNOR Z15CN16-02, BS 431S29, BS 321S31, BS 7S80, UNI X16CrNi16, SS 2321, AISI 431, SAE 431, JIS SUS431, EN X17CrNi16-2, EN 1.4057, ISO X17CrNi16-2, ISO C3, GOST 20Ch17N2, AMS 5628, ASTM MT431, ASTM 431, UNS S43100
IS 6603 Grade 15Cr16Ni2 general
| Property |
Temperature |
Value |
Comment |
| Density |
20.0 °C |
Density of 7.6 - 7.7 g/cm³ |
Typical for Martensitic Stainless Steel |
IS 6603 Grade 15Cr16Ni2 thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
20.0 °C |
Coefficient of thermal expansion of 1E-5 - 1.5E-5 1/K |
Typical for Martensitic Stainless Steel |
| Melting point |
- |
Melting point of 1375 - 1450 °C |
Typical for Martensitic Stainless Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 460 J/(kg·K) |
Typical for Martensitic Stainless Steel |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 14 - 31 W/(m·K) |
Typical for Martensitic Stainless Steel |
IS 6603 Grade 15Cr16Ni2 chemical
| Property |
Value |
| Carbon |
Carbon of 0.1 - 0.2 % |
| Chromium |
Chromium of 15 - 18 % |
| Iron |
Balance |
| Nickel |
Nickel of 1.5 - 3 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.03 % |
IS 6603 Grade 15Cr16Ni2 electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 6E-7 Ω·m |
Typical for Martensitic Stainless Steel |
IS 6603 Grade 15Cr16Ni2 mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 220 GPa |
Typical for Martensitic Stainless Steel |
| Elongation |
20.0 °C |
Elongation of 10 % |
- |
| Hardness, Brinell |
20.0 °C |
Hardness, Brinell of 342 [-] |
Annealed |
| Impact strength, Charpy notched |
20.0 °C |
Impact strength, Charpy notched of 31 kJ/m² |
Annealed |
| Poisson's ratio |
20.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Martensitic Stainless Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 830 - 1030 MPa |
Hardened and Tempered |
| Yield strength |
20.0 °C |
Yield strength of 640 MPa |
Hardened and Tempered |