EN 10346 Grade DX54D hit dip zinc coated (+Z)
EN 10346 Grade DX54D hit dip zinc coated (+Z) introduction
ArcelorMittal's hot dip galvanised steel consists of a steel substrate with a metallic zinc coating applied by means of a continuous hot dip galvanising process. Metallic zinc coatings are available in steel grades ranging from steel for bending and deep drawing applications, to structural steels and high yield strength steels.
A glossy surface finish obtained under specific skin-pass conditions (either non-skin-passed or skin-passed with smooth cylinders to obtain low roughness) can be provided if required at time of enquiry.
This Hot dip galvanised product offer excellent corrosion resistance combined with very good forming properties. The coating process can apply very thick zinc layers, up to 725 g/m² (total of both sides).
Equivalent material: EN FeP06G, DIN St 06Z, AFNOR GES, BS Z5 G, ASTM A653 Grade EDDS
EN 10346 Grade DX54D hit dip zinc coated (+Z) chemical
Property |
Value |
Comment |
Carbon |
Carbon of 0.12 % |
max. |
Manganese |
Manganese of 0.6 % |
max. |
Phosphorus |
Phosphorus of 0.1 % |
max. |
Silicon |
Silicon of 0.5 % |
max. |
Sulfur |
Sulfur of 0.045 % |
max. |
Titanium |
Titanium of 0.3 % |
max. |
EN 10346 Grade DX54D hit dip zinc coated (+Z) electrical
Property |
- |
- |
Application areas |
Coating |
Designation EN 10346 |
Coating weight - double sided (g/m²) |
Coating thickness (µm per side) |
Z100 |
100 |
7.0 |
Z140 |
140 |
10.0 |
Z200 |
200 |
14.0 |
Z225 |
225 |
16.0 |
Z275 |
275 |
20.0 |
Z350 |
350 |
25.0 |
Z450 |
450 |
31.0 |
Z600 |
600 |
42.0 |
Not included in the standard |
Z80 |
80 |
5.5 |
Z725 |
725 |
51.0 |
|
EN 10346 Grade DX54D hit dip zinc coated (+Z) mechanical
Property |
Value |
Comment |
Elongation |
Elongation of 32 % |
min. | for thickness 0.3-0.5 mm | Transverse | A80 |
- |
Elongation of 34 % |
min. | for thickness 0.5-0.7 mm | Transverse | A80 |
- |
Elongation of 36 % |
min. | for thickness 0.7-3 mm | Transverse | A80 |
Plastic strain ratio |
Plastic strain ratio of 1.2 [-] |
min. | 90ᵒ Transverse | for thickness 2-3 mm |
- |
Plastic strain ratio of 1.4 [-] |
min. | 90ᵒ Transverse | for thickness 1.5-2 mm |
- |
Plastic strain ratio of 1.6 [-] |
min. | 90ᵒ Transverse | for thickness 0.3-1.5 mm |
Strain hardening exponent |
Strain hardening exponent of 0.18 [-] |
min. | 90ᵒ Transverse | for thickness 0.3-3 mm |
Tensile strength |
Tensile strength of 260 - 350 MPa |
for thickness 0.3-3 mm | Transverse |
Yield strength |
Yield strength of 120 - 220 MPa |
for thickness 0.3-3 mm | Transverse |