EN 10327 Grade DX54D hot dip aluminium-silicon coated (+AS)
Equivalent material: JIS SGCD3, ASTM DDS, ASTM DS, GB DX54D, IS GPED, ISO 05, JIS SGCD1, ASTM A875DDS, ASTM A1046DDS, DIN 1.0306, DIN St 06 Z, DIN DX54D, AFNOR DX54D, BS DX54D, UNI FeP06G, JIS SGCMD3, JIS SZACD3, JIS SZACD4, EN 1.0306, GOST 05, GB/T DX54D
EN 10327 Grade DX54D hot dip aluminium-silicon coated (+AS) general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
EN 10327 Grade DX54D hot dip aluminium-silicon coated (+AS) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
EN 10327 Grade DX54D hot dip aluminium-silicon coated (+AS) chemical
| Property |
Value |
| Carbon |
Carbon of 0.12 % |
| Manganese |
Manganese of 0.6 % |
| Phosphorus |
Phosphorus of 0.1 % |
| Silicon |
Silicon of 0.5 % |
| Sulfur |
Sulfur of 0.045 % |
| Titanium |
Titanium of 0.3 % |
EN 10327 Grade DX54D hot dip aluminium-silicon coated (+AS) magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
EN 10327 Grade DX54D hot dip aluminium-silicon coated (+AS) electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
EN 10327 Grade DX54D hot dip aluminium-silicon coated (+AS) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Elongation A80, transverse |
20.0 °C |
Elongation A80, transverse of 27 - 34 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |