EN 10327 Grade DX52D hot dip zinc, zinc-iron, zinc-aluminium, zinc-magnesium, aluminium-zinc or aluminium-silicon coated
Equivalent material: GB DX52D, IS GPD, JIS SGCC, JIS SGCH, JIS SGCD1, ASTM A875FSTypeA, ASTM FSTypeA, ASTM TypeA, ASTM A1046FSTypeA, DIN 1.0350, DIN St 03 Z, DIN DX52D, AFNOR GE, AFNOR DX52D, BS DX52D, UNI FeP03G, JIS SGCD2, EN 1.0350, ISO 03, GOST 03, GB/T DX52D
EN 10327 Grade DX52D hot dip zinc, zinc-iron, zinc-aluminium, zinc-magnesium, aluminium-zinc or aluminium-silicon coated general
| Property |
Temperature |
Value |
Comment |
| Density |
20.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
EN 10327 Grade DX52D hot dip zinc, zinc-iron, zinc-aluminium, zinc-magnesium, aluminium-zinc or aluminium-silicon coated thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
20.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
EN 10327 Grade DX52D hot dip zinc, zinc-iron, zinc-aluminium, zinc-magnesium, aluminium-zinc or aluminium-silicon coated chemical
| Property |
Value |
| Carbon |
Carbon of 0.12 % |
| Manganese |
Manganese of 0.6 % |
| Phosphorus |
Phosphorus of 0.1 % |
| Silicon |
Silicon of 0.5 % |
| Sulfur |
Sulfur of 0.045 % |
| Titanium |
Titanium of 0.3 % |
EN 10327 Grade DX52D hot dip zinc, zinc-iron, zinc-aluminium, zinc-magnesium, aluminium-zinc or aluminium-silicon coated electrical
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
EN 10327 Grade DX52D hot dip zinc, zinc-iron, zinc-aluminium, zinc-magnesium, aluminium-zinc or aluminium-silicon coated mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Elongation A80, transverse |
20.0 °C |
Elongation A80, transverse of 19 - 26 % |
- |
| Poisson's ratio |
20.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Tensile strength, transverse |
20.0 °C |
Tensile strength, transverse of 270 - 420 MPa |
- |
| Yield strength, transverse |
20.0 °C |
Yield strength, transverse of 140 - 300 MPa |
- |