EN 10297-1 Grade 36Mn4 quenched and tempered (+QT)
Equivalent material: EN 36Mn4, DIN 1.0561, EN 1.0561
EN 10297-1 Grade 36Mn4 quenched and tempered (+QT) general
| Property | Temperature | Value |
|---|---|---|
| Density | 20.0 °C | Density of 7.82 - 7.85 g/cm³ |
EN 10297-1 Grade 36Mn4 quenched and tempered (+QT) thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Coefficient of thermal expansion | -100.0 °C | Coefficient of thermal expansion of 1.08E-5 1/K | - |
| - | 20.0 °C | Coefficient of thermal expansion of 1.19E-5 1/K | - |
| - | 100.0 °C | Coefficient of thermal expansion of 1.11E-5 - 1.25E-5 1/K | - |
| - | 200.0 °C | Coefficient of thermal expansion of 1.21E-5 - 1.3E-5 1/K | - |
| - | 300.0 °C | Coefficient of thermal expansion of 1.29E-5 - 1.36E-5 1/K | - |
| - | 400.0 °C | Coefficient of thermal expansion of 1.35E-5 - 1.41E-5 1/K | - |
| - | 500.0 °C | Coefficient of thermal expansion of 1.45E-5 1/K | - |
| - | 600.0 °C | Coefficient of thermal expansion of 1.49E-5 1/K | - |
| Max service temperature | - | Max service temperature of 500 °C | Typical for Carbon Steel |
| Melting point | - | Melting point of 1480 - 1526 °C | Typical for Low Carbon Steel |
| Specific heat capacity | -100.0 °C | Specific heat capacity of 423 J/(kg·K) | - |
| - | 20.0 °C | Specific heat capacity of 460 - 461 J/(kg·K) | - |
| - | 100.0 °C | Specific heat capacity of 479 J/(kg·K) | - |
| - | 200.0 °C | Specific heat capacity of 499 J/(kg·K) | - |
| - | 300.0 °C | Specific heat capacity of 517 J/(kg·K) | - |
| - | 400.0 °C | Specific heat capacity of 536 J/(kg·K) | - |
| - | 500.0 °C | Specific heat capacity of 558 J/(kg·K) | - |
| - | 600.0 °C | Specific heat capacity of 587 J/(kg·K) | - |
| Thermal conductivity | 20.0 °C | Thermal conductivity of 48 - 50 W/(m·K) | - |
| - | 100.0 °C | Thermal conductivity of 48.9 - 51 W/(m·K) | - |
| - | 200.0 °C | Thermal conductivity of 47.5 - 48.2 W/(m·K) | - |
| - | 300.0 °C | Thermal conductivity of 44.7 - 45.6 W/(m·K) | - |
| - | 400.0 °C | Thermal conductivity of 41.6 W/(m·K) | - |
| - | 500.0 °C | Thermal conductivity of 38.6 W/(m·K) | - |
| - | 600.0 °C | Thermal conductivity of 35.5 W/(m·K) | - |
| Thermal diffusivity | 20.0 °C | Thermal diffusivity of 13.3 mm²/s | - |
| - | 100.0 °C | Thermal diffusivity of 12.6 mm²/s | - |
| - | 200.0 °C | Thermal diffusivity of 11.5 mm²/s | - |
| - | 300.0 °C | Thermal diffusivity of 10.2 mm²/s | - |
| - | 400.0 °C | Thermal diffusivity of 8.9 mm²/s | - |
| - | 500.0 °C | Thermal diffusivity of 7.5 mm²/s | - |
| - | 600.0 °C | Thermal diffusivity of 6 mm²/s | - |
EN 10297-1 Grade 36Mn4 quenched and tempered (+QT) chemical
| Property | Value |
|---|---|
| Carbon | Carbon of 0.32 - 0.4 % |
| Manganese | Manganese of 0.9 - 1.2 % |
| Phosphorus | Phosphorus of 0.04 % |
| Silicon | Silicon of 0.4 % |
| Sulfur | Sulfur of 0.04 % |
EN 10297-1 Grade 36Mn4 quenched and tempered (+QT) magnetic
| Property | Value | Comment |
|---|---|---|
| Curie temperature | Curie temperature of 770 °C | Typical for Low Carbon Steel |
EN 10297-1 Grade 36Mn4 quenched and tempered (+QT) electrical
| Property | Temperature | Value |
|---|---|---|
| Electrical resistivity | 20.0 °C | Electrical resistivity of 1.2E-7 - 2.17E-7 Ω·m |
| - | 100.0 °C | Electrical resistivity of 2.62E-7 Ω·m |
| - | 200.0 °C | Electrical resistivity of 3.32E-7 Ω·m |
| - | 300.0 °C | Electrical resistivity of 4.2E-7 Ω·m |
| - | 400.0 °C | Electrical resistivity of 5.23E-7 Ω·m |
| - | 500.0 °C | Electrical resistivity of 6.41E-7 Ω·m |
| - | 600.0 °C | Electrical resistivity of 7.8E-7 Ω·m |
EN 10297-1 Grade 36Mn4 quenched and tempered (+QT) mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Elastic modulus | -100.0 °C | Elastic modulus of 217 GPa | - |
| - | 20.0 °C | Elastic modulus of 210 - 212 GPa | - |
| - | 100.0 °C | Elastic modulus of 205 - 207 GPa | - |
| - | 200.0 °C | Elastic modulus of 195 - 199 GPa | - |
| - | 300.0 °C | Elastic modulus of 185 - 192 GPa | - |
| - | 400.0 °C | Elastic modulus of 175 - 184 GPa | - |
| - | 500.0 °C | Elastic modulus of 175 GPa | - |
| - | 600.0 °C | Elastic modulus of 164 GPa | - |
| Elongation | 20.0 °C | Elongation of 13 - 15 % | - |
| Elongation, transverse | 20.0 °C | Elongation, transverse of 11 - 13 % | - |
| Poisson's ratio | 23.0 °C | Poisson's ratio of 0.29 [-] | Typical for Low Carbon Steel |
| Reduction of area | 20.0 °C | Reduction of area of 40 - 50 % | - |
| Reduction of area, transverse | 20.0 °C | Reduction of area, transverse of 40 - 50 % | - |
| Shear modulus | 20.0 °C | Shear modulus of 81 GPa | - |
| Tensile strength | 20.0 °C | Tensile strength of 600 - 1000 MPa | - |
| Tensile strength, transverse | 20.0 °C | Tensile strength, transverse of 600 - 1000 MPa | - |
| Yield strength | 20.0 °C | Yield strength of 400 - 550 MPa | - |
| Yield strength, transverse | 20.0 °C | Yield strength, transverse of 400 - 550 MPa | - |