EN 10277-5 Grade 42CrMo4 cold drawn or turned and quenched and tempered
EN 10277-5 Grade 42CrMo4 cold drawn or turned and quenched and tempered introduction
Steel 42 CrMo 4 is suitable for high loaded parts (also heavy forged parts) of high wear resistance and very favorable core qualities (e.g. crankshafts, pinions, balancer shafts) in vehicle manufacturing, engine and machine engineering. The steel has a high specific static and dynamic load resistance. Lowest application temp. -40 °C.
Equivalent material: NBN 42CrMo4, GB 42CrMo, AFNOR 42CD4, BS 708M40, GOST 38ChM, ISO 42CrMo4, UNI 42CrMo4, JIS SCM440, UNE F.1252-40CrMo4, ASTM 4140, DIN 1.7231, DIN GS-42CrMo4, EN 42CrMo4, EN 1.7231, DIN 1.7225, DIN 42CrMo4V, DIN 41CrMo4V, BS 709M40, BS EN19, SS 2244, UNE 42CrMo4, UNE F.125, AISI 4140, AISI 4140H, AISI 4142H, AISI 4142, AISI 4145, AISI NV-7, SAE 4140, SAE 4140H, SAE 4142H, SAE 4142, SAE 4145, SAE NV-7, JIS SCM440M, JIS SCM440H, JIS SNB7, EN 42CrMo4V, EN 41CrMo4V, EN 1.7225, GB/T 42CrMo, GB/T A30425, ASTM 4140H, ASTM 4142H, ASTM 4145, ASTM Grade B7, ASTM Grade B7M, ASTM Grade 12, ASTM Grade 7M, ASTM Grade L7, UNS G41400, UNS H41400, UNS H41420, UNS G41420, UNS G41450, IS 40Cr1Mo28
EN 10277-5 Grade 42CrMo4 cold drawn or turned and quenched and tempered general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.83 g/cm³ |
EN 10277-5 Grade 42CrMo4 cold drawn or turned and quenched and tempered thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
-100.0 °C |
Coefficient of thermal expansion of 1.05E-5 1/K |
- |
| - |
20.0 °C |
Coefficient of thermal expansion of 1.15E-5 1/K |
- |
| - |
100.0 °C |
Coefficient of thermal expansion of 1.21E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.27E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.32E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.36E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.4E-5 1/K |
- |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.44E-5 1/K |
- |
| Max service temperature, long |
- |
Max service temperature, long of -40 - 0 °C |
- |
| Melting point |
- |
Melting point of 1382 - 1529 °C |
Typical for Chromium Molybdenum Steel |
| Specific heat capacity |
-100.0 °C |
Specific heat capacity of 423 J/(kg·K) |
- |
| - |
20.0 °C |
Specific heat capacity of 461 J/(kg·K) |
- |
| - |
100.0 °C |
Specific heat capacity of 479 J/(kg·K) |
- |
| - |
200.0 °C |
Specific heat capacity of 499 J/(kg·K) |
- |
| - |
300.0 °C |
Specific heat capacity of 517 J/(kg·K) |
- |
| - |
400.0 °C |
Specific heat capacity of 536 J/(kg·K) |
- |
| - |
500.0 °C |
Specific heat capacity of 558 J/(kg·K) |
- |
| - |
600.0 °C |
Specific heat capacity of 587 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 45.1 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 45.1 W/(m·K) |
- |
| - |
200.0 °C |
Thermal conductivity of 44.1 W/(m·K) |
- |
| - |
300.0 °C |
Thermal conductivity of 41.9 W/(m·K) |
- |
| - |
400.0 °C |
Thermal conductivity of 39.4 W/(m·K) |
- |
| - |
500.0 °C |
Thermal conductivity of 36.9 W/(m·K) |
- |
| - |
600.0 °C |
Thermal conductivity of 34.4 W/(m·K) |
- |
| Thermal diffusivity |
20.0 °C |
Thermal diffusivity of 12.5 mm²/s |
- |
| - |
100.0 °C |
Thermal diffusivity of 11.6 mm²/s |
- |
| - |
200.0 °C |
Thermal diffusivity of 10.6 mm²/s |
- |
| - |
300.0 °C |
Thermal diffusivity of 9.5 mm²/s |
- |
| - |
400.0 °C |
Thermal diffusivity of 8.4 mm²/s |
- |
| - |
500.0 °C |
Thermal diffusivity of 7.1 mm²/s |
- |
| - |
600.0 °C |
Thermal diffusivity of 5.8 mm²/s |
- |
EN 10277-5 Grade 42CrMo4 cold drawn or turned and quenched and tempered chemical
| Property |
Value |
| Carbon |
Carbon of 0.38 - 0.45 % |
| Chromium |
Chromium of 0.9 - 1.2 % |
| Manganese |
Manganese of 0.6 - 0.9 % |
| Molybdenum |
Molybdenum of 0.15 - 0.3 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 0.4 % |
| Sulfur |
Sulfur of 0.03 % |
EN 10277-5 Grade 42CrMo4 cold drawn or turned and quenched and tempered electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 2.31E-7 Ω·m |
| - |
100.0 °C |
Electrical resistivity of 2.84E-7 Ω·m |
| - |
200.0 °C |
Electrical resistivity of 3.58E-7 Ω·m |
| - |
300.0 °C |
Electrical resistivity of 4.48E-7 Ω·m |
| - |
400.0 °C |
Electrical resistivity of 5.52E-7 Ω·m |
| - |
500.0 °C |
Electrical resistivity of 6.71E-7 Ω·m |
| - |
600.0 °C |
Electrical resistivity of 8.06E-7 Ω·m |
EN 10277-5 Grade 42CrMo4 cold drawn or turned and quenched and tempered mechanical
| Property |
Temperature |
Value |
| Elastic modulus |
-100.0 °C |
Elastic modulus of 217 GPa |
| - |
20.0 °C |
Elastic modulus of 212 GPa |
| - |
100.0 °C |
Elastic modulus of 207 GPa |
| - |
200.0 °C |
Elastic modulus of 199 GPa |
| - |
300.0 °C |
Elastic modulus of 192 GPa |
| - |
400.0 °C |
Elastic modulus of 184 GPa |
| - |
500.0 °C |
Elastic modulus of 175 GPa |
| - |
600.0 °C |
Elastic modulus of 164 GPa |
| Elongation |
20.0 °C |
Elongation of 10 - 12 % |
| Poisson's ratio |
20.0 °C |
Poisson's ratio of 0.28 [-] |
| Reduction of area |
20.0 °C |
Reduction of area of 40 - 50 % |
| Tensile strength |
20.0 °C |
Tensile strength of 900 - 1300 MPa |
| Yield strength |
20.0 °C |
Yield strength of 650 - 900 MPa |