EN 10269 Grade 42CrMo4 annealed to achieve spheroidized carbides (+AC)
EN 10269 Grade 42CrMo4 annealed to achieve spheroidized carbides (+AC) introduction
Steel 42CrMo4 is suitable for high-stress components (also large forged parts) in vehicle, engine and machine engineering with high wear resistance and very favorable core properties ( e.g. crankshafts, pinions, balance shafts). The steel shows a high resistivity to static and dynamic loading.
Lowest working temperature -40 °C
Further application for mounting elements at increased and lower temperatures.
Equivalent material: NBN 42CrMo4, GB 42CrMo, AFNOR 42CD4, BS 708M40, GOST 38ChM, ISO 42CrMo4, UNI 42CrMo4, JIS SCM440, SS 2244, UNE F.1252-40CrMo4, ASTM 4140, DIN 42CrMo4, IS 43Cr4Mo2, JIS SNB7 Class 2, ASTM B7, ASTM B7M, ASTM L7, UNS G41400, GB A30422, DIN GC, ASTM A193 Grade B7, ASTM A193 Grade B7M, ASTM A320 Grade L7, ASTM A320 Grade L7M, UNS H41400, DIN 1.7231, DIN GS-42CrMo4, EN 1.7231, DIN 1.7225, DIN 42CrMo4V, DIN 41CrMo4V, BS 709M40, BS EN19, UNE 42CrMo4, UNE F.125, AISI 4140, AISI 4140H, AISI 4142H, AISI 4142, AISI 4145, AISI NV-7, SAE 4140, SAE 4140H, SAE 4142H, SAE 4142, SAE 4145, SAE NV-7, JIS SCM440M, JIS SCM440H, JIS SNB7, EN 42CrMo4V, EN 41CrMo4V, EN 1.7225, GB/T 42CrMo, GB/T A30425, ASTM 4140H, ASTM 4142H, ASTM 4145, ASTM Grade B7, ASTM Grade B7M, ASTM Grade 12, ASTM Grade 7M, ASTM Grade L7, UNS H41420, UNS G41420, UNS G41450, IS 40Cr1Mo28
EN 10269 Grade 42CrMo4 annealed to achieve spheroidized carbides (+AC) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.83 - 7.85 g/cm³ |
EN 10269 Grade 42CrMo4 annealed to achieve spheroidized carbides (+AC) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
-100.0 °C |
Coefficient of thermal expansion of 1.05E-5 1/K |
- |
| - |
20.0 °C |
Coefficient of thermal expansion of 1.15E-5 1/K |
- |
| - |
100.0 °C |
Coefficient of thermal expansion of 1.11E-5 - 1.21E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.21E-5 - 1.27E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.29E-5 - 1.32E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.35E-5 - 1.36E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.4E-5 1/K |
- |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.44E-5 1/K |
- |
| Max service temperature, long |
- |
Max service temperature, long of -40 - 0 °C |
- |
| Melting point |
- |
Melting point of 1382 - 1529 °C |
Typical for Chromium Molybdenum Steel |
| Specific heat capacity |
-100.0 °C |
Specific heat capacity of 423 J/(kg·K) |
- |
| - |
20.0 °C |
Specific heat capacity of 461 J/(kg·K) |
- |
| - |
100.0 °C |
Specific heat capacity of 479 J/(kg·K) |
- |
| - |
200.0 °C |
Specific heat capacity of 499 J/(kg·K) |
- |
| - |
300.0 °C |
Specific heat capacity of 517 J/(kg·K) |
- |
| - |
400.0 °C |
Specific heat capacity of 536 J/(kg·K) |
- |
| - |
500.0 °C |
Specific heat capacity of 558 J/(kg·K) |
- |
| - |
600.0 °C |
Specific heat capacity of 587 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 45.1 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 45.1 W/(m·K) |
- |
| - |
200.0 °C |
Thermal conductivity of 44.1 W/(m·K) |
- |
| - |
300.0 °C |
Thermal conductivity of 41.9 W/(m·K) |
- |
| - |
400.0 °C |
Thermal conductivity of 39.4 W/(m·K) |
- |
| - |
500.0 °C |
Thermal conductivity of 36.9 W/(m·K) |
- |
| - |
600.0 °C |
Thermal conductivity of 34.4 W/(m·K) |
- |
| Thermal diffusivity |
20.0 °C |
Thermal diffusivity of 12.5 mm²/s |
- |
| - |
100.0 °C |
Thermal diffusivity of 11.6 mm²/s |
- |
| - |
200.0 °C |
Thermal diffusivity of 10.6 mm²/s |
- |
| - |
300.0 °C |
Thermal diffusivity of 9.5 mm²/s |
- |
| - |
400.0 °C |
Thermal diffusivity of 8.4 mm²/s |
- |
| - |
500.0 °C |
Thermal diffusivity of 7.1 mm²/s |
- |
| - |
600.0 °C |
Thermal diffusivity of 5.8 mm²/s |
- |
EN 10269 Grade 42CrMo4 annealed to achieve spheroidized carbides (+AC) chemical
| Property |
Value |
| Carbon |
Carbon of 0.38 - 0.45 % |
| Chromium |
Chromium of 0.9 - 1.2 % |
| Manganese |
Manganese of 0.6 - 0.9 % |
| Molybdenum |
Molybdenum of 0.15 - 0.3 % |
| Phosphorus |
Phosphorus of 0.03 - 0.04 % |
| Silicon |
Silicon of 0.4 % |
| Sulfur |
Sulfur of 0.035 % |
EN 10269 Grade 42CrMo4 annealed to achieve spheroidized carbides (+AC) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 2.31E-7 Ω·m |
| - |
100.0 °C |
Electrical resistivity of 2.84E-7 Ω·m |
| - |
200.0 °C |
Electrical resistivity of 3.58E-7 Ω·m |
| - |
300.0 °C |
Electrical resistivity of 4.48E-7 Ω·m |
| - |
400.0 °C |
Electrical resistivity of 5.52E-7 Ω·m |
| - |
500.0 °C |
Electrical resistivity of 6.71E-7 Ω·m |
| - |
600.0 °C |
Electrical resistivity of 8.06E-7 Ω·m |
EN 10269 Grade 42CrMo4 annealed to achieve spheroidized carbides (+AC) mechanical
| Property |
Temperature |
Value |
| Elastic modulus |
-100.0 °C |
Elastic modulus of 217 GPa |
| - |
20.0 °C |
Elastic modulus of 212 GPa |
| - |
100.0 °C |
Elastic modulus of 205 - 207 GPa |
| - |
200.0 °C |
Elastic modulus of 195 - 199 GPa |
| - |
300.0 °C |
Elastic modulus of 185 - 192 GPa |
| - |
400.0 °C |
Elastic modulus of 184 GPa |
| - |
500.0 °C |
Elastic modulus of 175 GPa |
| - |
600.0 °C |
Elastic modulus of 164 GPa |
| Poisson's ratio |
20.0 °C |
Poisson's ratio of 0.28 [-] |
| Reduction of area |
20.0 °C |
Reduction of area of 57 % |
| Tensile strength |
20.0 °C |
Tensile strength of 630 MPa |
Trust our high-quality steel to forge a brighter and stronger future for your projects.