EN 10277-3 Grade 11SMn37 as rolled and turned (+SH)
EN 10277-3 Grade 11SMn37 as rolled and turned (+SH) introduction
Free cutting steel 11SMn37 is unsuitable for heat-treatment and is preferred steel 11SMn30 for higher requirements to machinability and surface appearance due to its higher S-content. For lower machinability demands it replaces the Pb-alloyed steel 11SMn30. Increased cracking sensitivity has to be considered. Therefore limited application for bulk parts in car industry as well as in apparatus and equipment engineering. As a bright steel product it is used in the form of bars, bright, straight, in various conditions (see DIN EN 10277 : 1999-10).
Equivalent material: AFNOR S300, BS 240M07, ISO 12SMn35, UNI CF9SMn36, JIS SUM25, SS 1912-04, VSM 9SMn36, UNE F.2113-12SMn35, SAE 1215, DIN 9SMn36, ISO 11SMn37, ASTM A108 Grade 1215, UNS G12150, DIN 1.0736, DIN 11SMn37, AFNOR 11SMn37, BS 11SMn37, AISI 1215, JIS 12SMn35, EN 1.0736, ASTM 1215
EN 10277-3 Grade 11SMn37 as rolled and turned (+SH) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.83 - 7.85 g/cm³ |
EN 10277-3 Grade 11SMn37 as rolled and turned (+SH) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
-100.0 °C |
Coefficient of thermal expansion of 1.08E-5 1/K |
- |
| - |
20.0 °C |
Coefficient of thermal expansion of 1.19E-5 1/K |
- |
| - |
100.0 °C |
Coefficient of thermal expansion of 1.1E-5 - 1.25E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.18E-5 - 1.3E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.36E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.41E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.45E-5 1/K |
- |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.49E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
-100.0 °C |
Specific heat capacity of 423 J/(kg·K) |
- |
| - |
20.0 °C |
Specific heat capacity of 460 - 461 J/(kg·K) |
- |
| - |
100.0 °C |
Specific heat capacity of 479 - 480 J/(kg·K) |
- |
| - |
200.0 °C |
Specific heat capacity of 499 - 520 J/(kg·K) |
- |
| - |
300.0 °C |
Specific heat capacity of 517 J/(kg·K) |
- |
| - |
400.0 °C |
Specific heat capacity of 536 - 610 J/(kg·K) |
- |
| - |
500.0 °C |
Specific heat capacity of 558 J/(kg·K) |
- |
| - |
600.0 °C |
Specific heat capacity of 587 J/(kg·K) |
- |
| Thermal conductivity |
-100.0 °C |
Thermal conductivity of 37.6 W/(m·K) |
- |
| - |
20.0 °C |
Thermal conductivity of 42.2 - 54.4 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 43.2 W/(m·K) |
- |
| - |
200.0 °C |
Thermal conductivity of 42.9 W/(m·K) |
- |
| - |
300.0 °C |
Thermal conductivity of 41.2 W/(m·K) |
- |
| - |
400.0 °C |
Thermal conductivity of 39.1 W/(m·K) |
- |
| - |
500.0 °C |
Thermal conductivity of 36.6 W/(m·K) |
- |
| - |
600.0 °C |
Thermal conductivity of 34.1 W/(m·K) |
- |
| Thermal diffusivity |
-100.0 °C |
Thermal diffusivity of 12.9 mm²/s |
- |
| - |
20.0 °C |
Thermal diffusivity of 11.7 mm²/s |
- |
| - |
100.0 °C |
Thermal diffusivity of 11.2 mm²/s |
- |
| - |
200.0 °C |
Thermal diffusivity of 10.3 mm²/s |
- |
| - |
300.0 °C |
Thermal diffusivity of 9.4 mm²/s |
- |
| - |
400.0 °C |
Thermal diffusivity of 8.3 mm²/s |
- |
| - |
500.0 °C |
Thermal diffusivity of 7.1 mm²/s |
- |
| - |
600.0 °C |
Thermal diffusivity of 5.7 mm²/s |
- |
EN 10277-3 Grade 11SMn37 as rolled and turned (+SH) chemical
| Property |
Value |
| Carbon |
Carbon of 0.14 % |
| Manganese |
Manganese of 1 - 1.5 % |
| Phosphorus |
Phosphorus of 0.11 % |
| Silicon |
Silicon of 0.05 % |
| Sulfur |
Sulfur of 0.34 - 0.4 % |
EN 10277-3 Grade 11SMn37 as rolled and turned (+SH) magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
EN 10277-3 Grade 11SMn37 as rolled and turned (+SH) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
-100.0 °C |
Electrical resistivity of 1.82E-7 Ω·m |
| - |
20.0 °C |
Electrical resistivity of 1.1E-7 - 2.47E-7 Ω·m |
| - |
100.0 °C |
Electrical resistivity of 2.96E-7 Ω·m |
| - |
200.0 °C |
Electrical resistivity of 3.68E-7 Ω·m |
| - |
300.0 °C |
Electrical resistivity of 4.55E-7 Ω·m |
| - |
400.0 °C |
Electrical resistivity of 5.56E-7 Ω·m |
| - |
500.0 °C |
Electrical resistivity of 6.75E-7 Ω·m |
| - |
600.0 °C |
Electrical resistivity of 8.13E-7 Ω·m |
EN 10277-3 Grade 11SMn37 as rolled and turned (+SH) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
-100.0 °C |
Elastic modulus of 217 GPa |
- |
| - |
20.0 °C |
Elastic modulus of 210 - 212 GPa |
- |
| - |
100.0 °C |
Elastic modulus of 207 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 193 - 199 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 185 - 192 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 175 - 184 GPa |
- |
| - |
500.0 °C |
Elastic modulus of 175 GPa |
- |
| - |
600.0 °C |
Elastic modulus of 164 GPa |
- |
| Hardness, Brinell |
20.0 °C |
Hardness, Brinell of 107 - 169 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
20.0 °C |
Shear modulus of 81 GPa |
- |
| Tensile strength |
20.0 °C |
Tensile strength of 360 - 570 MPa |
- |
Build a solid foundation for success with our reliable and robust steel products.