EN 10277-2 Grade E295GC cold drawn
EN 10277-2 Grade E295GC cold drawn introduction
E295GC is applicated as cold drawing grade. The steel is used for wear and strength loaded parts (bolts, shafts, spindles, wedges). As a bright steel product it is used in the form of bars, bright, straight, in various conditions (see DIN EN 10277 : 1999-10).
Equivalent material: DIN ZSt50-2, DIN 1.0533, DIN E295GC, AFNOR E295GC, BS E295GC, JIS SS490, EN 1.0533, ISO Fe 490, GB Q275B, ASTM Grade A
EN 10277-2 Grade E295GC cold drawn general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.85 g/cm³ |
EN 10277-2 Grade E295GC cold drawn thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
100.0 °C |
Coefficient of thermal expansion of 1.11E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.21E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.29E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.35E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1380 - 1514 °C |
Typical for Medium Carbon Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 450 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 54 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 50.7 W/(m·K) |
- |
| - |
200.0 °C |
Thermal conductivity of 46.9 W/(m·K) |
- |
| - |
300.0 °C |
Thermal conductivity of 41.5 W/(m·K) |
- |
| - |
400.0 °C |
Thermal conductivity of 39.4 W/(m·K) |
- |
EN 10277-2 Grade E295GC cold drawn magnetic
| Property |
Value |
| Nitrogen |
Nitrogen of 9E-3 % |
| Phosphorus |
Phosphorus of 0.05 % |
| Sulfur |
Sulfur of 0.045 % |
EN 10277-2 Grade E295GC cold drawn electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 2E-7 Ω·m |
EN 10277-2 Grade E295GC cold drawn mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 210 GPa |
- |
| - |
100.0 °C |
Elastic modulus of 205 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 195 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 185 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 175 GPa |
- |
| Elongation |
20.0 °C |
Elongation of 6 - 9 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Medium Carbon Steel |
| Shear modulus |
20.0 °C |
Shear modulus of 81 GPa |
- |
| Tensile strength |
20.0 °C |
Tensile strength of 470 - 950 MPa |
- |
| Yield strength Rp0.2 |
20.0 °C |
Yield strength Rp0.2 of 255 - 510 MPa |
- |
Our stringent quality control measures guarantee the highest standards of steel.