EN 10263-4 Grade 37Cr4 quenched and tempered (+QT)

EN 10263-4 Grade 37Cr4 quenched and tempered (+QT) introduction

The cold-upsettable steel 37 Cr 4 can be cold-formed with a medium to high rate of forming according to the usual forming methods on single-stage and multi-stage presses. It is used for screws of strength class 8.8 in the thick dimension range.

Equivalent material: NBN 37Cr4, CSN 14140, AFNOR 38C4, BS 530M36, GOST 40Ch, ISO C15, UNI 38Cr4KB, JIS SCr435, PN 38HA, UNE F.1210-38Cr4DF, ASTM 5135, DIN 1.7034, AFNOR 37Cr4, BS 37Cr4, AISI 5132, AISI 5135H, SAE 5132, SAE 5135H, JIS SCr435WCH, JIS SCr435H, JIS SCr435M, JIS SCr435HRCH, EN 37Cr4, EN 1.7034, GOST 35X, GOST 38ChA, GOST SchCh10, UNS H51350, UNS G51320

EN 10263-4 Grade 37Cr4 quenched and tempered (+QT) general

Property Temperature Value
Density 20.0 °C Density of 7.83 g/cm³

EN 10263-4 Grade 37Cr4 quenched and tempered (+QT) thermal

Property Temperature Value Comment
Coefficient of thermal expansion -100.0 °C Coefficient of thermal expansion of 1.05E-5 1/K -
- 20.0 °C Coefficient of thermal expansion of 1.15E-5 1/K -
- 100.0 °C Coefficient of thermal expansion of 1.21E-5 1/K -
- 200.0 °C Coefficient of thermal expansion of 1.27E-5 1/K -
- 300.0 °C Coefficient of thermal expansion of 1.32E-5 1/K -
- 400.0 °C Coefficient of thermal expansion of 1.36E-5 1/K -
- 500.0 °C Coefficient of thermal expansion of 1.4E-5 1/K -
- 600.0 °C Coefficient of thermal expansion of 1.44E-5 1/K -
Melting point - Melting point of 1382 - 1529 °C Typical for Chromium Steel
Specific heat capacity -100.0 °C Specific heat capacity of 423 J/(kg·K) -
- 20.0 °C Specific heat capacity of 461 J/(kg·K) -
- 100.0 °C Specific heat capacity of 479 J/(kg·K) -
- 200.0 °C Specific heat capacity of 499 J/(kg·K) -
- 300.0 °C Specific heat capacity of 517 J/(kg·K) -
- 400.0 °C Specific heat capacity of 536 J/(kg·K) -
- 500.0 °C Specific heat capacity of 558 J/(kg·K) -
- 600.0 °C Specific heat capacity of 587 J/(kg·K) -
Thermal conductivity 20.0 °C Thermal conductivity of 45.1 W/(m·K) -
- 100.0 °C Thermal conductivity of 45.1 W/(m·K) -
- 200.0 °C Thermal conductivity of 44.1 W/(m·K) -
- 300.0 °C Thermal conductivity of 41.9 W/(m·K) -
- 400.0 °C Thermal conductivity of 39.4 W/(m·K) -
- 500.0 °C Thermal conductivity of 36.9 W/(m·K) -
- 600.0 °C Thermal conductivity of 34.4 W/(m·K) -
Thermal diffusivity 20.0 °C Thermal diffusivity of 12.5 mm²/s -
- 100.0 °C Thermal diffusivity of 11.6 mm²/s -
- 200.0 °C Thermal diffusivity of 10.6 mm²/s -
- 300.0 °C Thermal diffusivity of 9.5 mm²/s -
- 400.0 °C Thermal diffusivity of 8.4 mm²/s -
- 500.0 °C Thermal diffusivity of 7.1 mm²/s -
- 600.0 °C Thermal diffusivity of 5.8 mm²/s -

EN 10263-4 Grade 37Cr4 quenched and tempered (+QT) chemical

Property Value
Carbon Carbon of 0.34 - 0.41 %
Chromium Chromium of 0.9 - 1.2 %
Manganese Manganese of 0.6 - 0.9 %
Phosphorus Phosphorus of 0.04 %
Silicon Silicon of 0.4 %
Sulfur Sulfur of 0.035 %

EN 10263-4 Grade 37Cr4 quenched and tempered (+QT) electrical

Property Temperature Value
Electrical resistivity 20.0 °C Electrical resistivity of 2.31E-7 Ω·m
- 100.0 °C Electrical resistivity of 2.84E-7 Ω·m
- 200.0 °C Electrical resistivity of 3.58E-7 Ω·m
- 300.0 °C Electrical resistivity of 4.48E-7 Ω·m
- 400.0 °C Electrical resistivity of 5.52E-7 Ω·m
- 500.0 °C Electrical resistivity of 6.71E-7 Ω·m
- 600.0 °C Electrical resistivity of 8.06E-7 Ω·m

EN 10263-4 Grade 37Cr4 quenched and tempered (+QT) mechanical

Property Temperature Value
Elastic modulus -100.0 °C Elastic modulus of 217 GPa
- 20.0 °C Elastic modulus of 212 GPa
- 100.0 °C Elastic modulus of 207 GPa
- 200.0 °C Elastic modulus of 199 GPa
- 300.0 °C Elastic modulus of 192 GPa
- 400.0 °C Elastic modulus of 184 GPa
- 500.0 °C Elastic modulus of 175 GPa
- 600.0 °C Elastic modulus of 164 GPa
Elongation 20.0 °C Elongation of 11 - 13 %
Poisson's ratio 20.0 °C Poisson's ratio of 0.28 [-]
Reduction of area 20.0 °C Reduction of area of 35 - 40 %
Tensile strength 20.0 °C Tensile strength of 750 - 1150 MPa
Yield strength 20.0 °C Yield strength of 510 - 750 MPa