EN 10263-4 Grade 34Cr4 quenched and tempered (+QT)
EN 10263-4 Grade 34Cr4 quenched and tempered (+QT) introduction
The cold-upsettable steel 34 Cr 4 can be cold-formed with a medium to high rate of forming according to the usual forming methods on single-stage and multi-stage presses. It is used for hexagon screws and hexagon socket head cap screw of strength class 8.8 in the medium to thick dimension range and of strength class 10.9 in the thin to medium dimension range.
Equivalent material: NBN 34Cr4, AFNOR 32C4, BS 530M32, GOST 35Ch, ISO C14, UNI 34Cr4KB, JIS SCr430, PN 30H, ASTM 5132, DIN 1.7033, BS 530A32, SS 34Cr4(KB), UNE 35Cr4, AISI 5132, AISI 5132H, SAE 5132, SAE 5132H, JIS SCr430WCH, JIS SCr430H, EN 34Cr4, EN 1.7033, GB/T 35Cr, GB/T A20352, UNS H51320, UNS G51320
EN 10263-4 Grade 34Cr4 quenched and tempered (+QT) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.83 g/cm³ |
EN 10263-4 Grade 34Cr4 quenched and tempered (+QT) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
-100.0 °C |
Coefficient of thermal expansion of 1.05E-5 1/K |
- |
| - |
20.0 °C |
Coefficient of thermal expansion of 1.15E-5 1/K |
- |
| - |
100.0 °C |
Coefficient of thermal expansion of 1.21E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.27E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.32E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.36E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.4E-5 1/K |
- |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.44E-5 1/K |
- |
| Melting point |
- |
Melting point of 1382 - 1529 °C |
Typical for Chromium Steel |
| Specific heat capacity |
-100.0 °C |
Specific heat capacity of 423 J/(kg·K) |
- |
| - |
20.0 °C |
Specific heat capacity of 461 J/(kg·K) |
- |
| - |
100.0 °C |
Specific heat capacity of 479 J/(kg·K) |
- |
| - |
200.0 °C |
Specific heat capacity of 499 J/(kg·K) |
- |
| - |
300.0 °C |
Specific heat capacity of 517 J/(kg·K) |
- |
| - |
400.0 °C |
Specific heat capacity of 536 J/(kg·K) |
- |
| - |
500.0 °C |
Specific heat capacity of 558 J/(kg·K) |
- |
| - |
600.0 °C |
Specific heat capacity of 587 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 45.1 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 45.1 W/(m·K) |
- |
| - |
200.0 °C |
Thermal conductivity of 44.1 W/(m·K) |
- |
| - |
300.0 °C |
Thermal conductivity of 41.9 W/(m·K) |
- |
| - |
400.0 °C |
Thermal conductivity of 39.4 W/(m·K) |
- |
| - |
500.0 °C |
Thermal conductivity of 36.9 W/(m·K) |
- |
| - |
600.0 °C |
Thermal conductivity of 34.4 W/(m·K) |
- |
| Thermal diffusivity |
20.0 °C |
Thermal diffusivity of 12.5 mm²/s |
- |
| - |
100.0 °C |
Thermal diffusivity of 11.6 mm²/s |
- |
| - |
200.0 °C |
Thermal diffusivity of 10.6 mm²/s |
- |
| - |
300.0 °C |
Thermal diffusivity of 9.5 mm²/s |
- |
| - |
400.0 °C |
Thermal diffusivity of 8.4 mm²/s |
- |
| - |
500.0 °C |
Thermal diffusivity of 7.1 mm²/s |
- |
| - |
600.0 °C |
Thermal diffusivity of 5.8 mm²/s |
- |
EN 10263-4 Grade 34Cr4 quenched and tempered (+QT) chemical
| Property |
Value |
| Carbon |
Carbon of 0.3 - 0.37 % |
| Chromium |
Chromium of 0.9 - 1.2 % |
| Manganese |
Manganese of 0.6 - 0.9 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 0.4 % |
| Sulfur |
Sulfur of 0.035 % |
EN 10263-4 Grade 34Cr4 quenched and tempered (+QT) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 2.31E-7 Ω·m |
| - |
100.0 °C |
Electrical resistivity of 2.84E-7 Ω·m |
| - |
200.0 °C |
Electrical resistivity of 3.58E-7 Ω·m |
| - |
300.0 °C |
Electrical resistivity of 4.48E-7 Ω·m |
| - |
400.0 °C |
Electrical resistivity of 5.52E-7 Ω·m |
| - |
500.0 °C |
Electrical resistivity of 6.71E-7 Ω·m |
| - |
600.0 °C |
Electrical resistivity of 8.06E-7 Ω·m |
EN 10263-4 Grade 34Cr4 quenched and tempered (+QT) mechanical
| Property |
Temperature |
Value |
| Elastic modulus |
-100.0 °C |
Elastic modulus of 217 GPa |
| - |
20.0 °C |
Elastic modulus of 212 GPa |
| - |
100.0 °C |
Elastic modulus of 207 GPa |
| - |
200.0 °C |
Elastic modulus of 199 GPa |
| - |
300.0 °C |
Elastic modulus of 192 GPa |
| - |
400.0 °C |
Elastic modulus of 184 GPa |
| - |
500.0 °C |
Elastic modulus of 175 GPa |
| - |
600.0 °C |
Elastic modulus of 164 GPa |
| Elongation |
20.0 °C |
Elongation of 11 - 15 % |
| Poisson's ratio |
20.0 °C |
Poisson's ratio of 0.28 [-] |
| Reduction of area |
20.0 °C |
Reduction of area of 35 - 45 % |
| Tensile strength |
20.0 °C |
Tensile strength of 700 - 1100 MPa |
| Yield strength |
20.0 °C |
Yield strength of 460 - 700 MPa |