EN 10083-1 Grade 34Cr4 quenched and tempered (+QT)

EN 10083-1 Grade 34Cr4 quenched and tempered (+QT) introduction

Steel 34Cr4 is suitable for mean loaded parts and mean heat-treatment sections in vehicle manufacturing, engine and machine engineering (e.g. transmission parts, shafts, axles). Lowest working temperature -25 °C.

Equivalent material: NBN 34Cr4, GB 35Cr, AFNOR 32C4, BS 530M32, GOST 35Ch, ISO 34Cr4, UNI 34Cr4, JIS SCr430, PN 30H, ASTM 5132, ASTM 1536, SAE 1536, DIN 34Cr4, GB A20352, JIS SCr430H, GOST 35Г, KS SCr430H, ASTM A29 Grade 5132, ASTM A304 Grade 5132H, UNS H51320, EN 1.7033, DIN 1.7033, BS 530A32, SS 34Cr4(KB), UNE 35Cr4, AISI 5132, AISI 5132H, SAE 5132, SAE 5132H, JIS SCr430WCH, GB/T 35Cr, GB/T A20352, UNS G51320

EN 10083-1 Grade 34Cr4 quenched and tempered (+QT) general

Property Temperature Value
Density 20.0 °C Density of 7.83 - 7.85 g/cm³

EN 10083-1 Grade 34Cr4 quenched and tempered (+QT) thermal

Property Temperature Value Comment
Coefficient of thermal expansion -100.0 °C Coefficient of thermal expansion of 1.05E-5 1/K -
- 20.0 °C Coefficient of thermal expansion of 1.15E-5 1/K -
- 100.0 °C Coefficient of thermal expansion of 1.11E-5 - 1.21E-5 1/K -
- 200.0 °C Coefficient of thermal expansion of 1.21E-5 - 1.27E-5 1/K -
- 300.0 °C Coefficient of thermal expansion of 1.29E-5 - 1.32E-5 1/K -
- 400.0 °C Coefficient of thermal expansion of 1.35E-5 - 1.36E-5 1/K -
- 500.0 °C Coefficient of thermal expansion of 1.4E-5 1/K -
- 600.0 °C Coefficient of thermal expansion of 1.44E-5 1/K -
Max service temperature, long - Max service temperature, long of -25 - 0 °C -
Melting point - Melting point of 1382 - 1529 °C Typical for Chromium Steel
Specific heat capacity -100.0 °C Specific heat capacity of 423 J/(kg·K) -
- 20.0 °C Specific heat capacity of 460 - 461 J/(kg·K) -
- 100.0 °C Specific heat capacity of 479 J/(kg·K) -
- 200.0 °C Specific heat capacity of 499 J/(kg·K) -
- 300.0 °C Specific heat capacity of 517 J/(kg·K) -
- 400.0 °C Specific heat capacity of 536 J/(kg·K) -
- 500.0 °C Specific heat capacity of 558 J/(kg·K) -
- 600.0 °C Specific heat capacity of 587 J/(kg·K) -
Thermal conductivity 20.0 °C Thermal conductivity of 45.1 - 46 W/(m·K) -
- 100.0 °C Thermal conductivity of 45.1 W/(m·K) -
- 200.0 °C Thermal conductivity of 44.1 W/(m·K) -
- 300.0 °C Thermal conductivity of 41.9 W/(m·K) -
- 400.0 °C Thermal conductivity of 39.4 W/(m·K) -
- 500.0 °C Thermal conductivity of 36.9 W/(m·K) -
- 600.0 °C Thermal conductivity of 34.4 W/(m·K) -
Thermal diffusivity 20.0 °C Thermal diffusivity of 12.5 mm²/s -
- 100.0 °C Thermal diffusivity of 11.6 mm²/s -
- 200.0 °C Thermal diffusivity of 10.6 mm²/s -
- 300.0 °C Thermal diffusivity of 9.5 mm²/s -
- 400.0 °C Thermal diffusivity of 8.4 mm²/s -
- 500.0 °C Thermal diffusivity of 7.1 mm²/s -
- 600.0 °C Thermal diffusivity of 5.8 mm²/s -

EN 10083-1 Grade 34Cr4 quenched and tempered (+QT) chemical

Property Value
Carbon Carbon of 0.3 - 0.37 %
Chromium Chromium of 0.9 - 1.2 %
Copper Copper of 0.4 %
Manganese Manganese of 0.6 - 0.9 %
Phosphorus Phosphorus of 0.03 - 0.04 %
Silicon Silicon of 0.1 - 0.4 %
Sulfur Sulfur of 0.035 %

EN 10083-1 Grade 34Cr4 quenched and tempered (+QT) electrical

Property Temperature Value
Electrical resistivity 20.0 °C Electrical resistivity of 1.9E-7 - 2.31E-7 Ω·m
- 100.0 °C Electrical resistivity of 2.84E-7 Ω·m
- 200.0 °C Electrical resistivity of 3.58E-7 Ω·m
- 300.0 °C Electrical resistivity of 4.48E-7 Ω·m
- 400.0 °C Electrical resistivity of 5.52E-7 Ω·m
- 500.0 °C Electrical resistivity of 6.71E-7 Ω·m
- 600.0 °C Electrical resistivity of 8.06E-7 Ω·m

EN 10083-1 Grade 34Cr4 quenched and tempered (+QT) mechanical

Property Temperature Value
Elastic modulus -100.0 °C Elastic modulus of 217 GPa
- 20.0 °C Elastic modulus of 210 - 212 GPa
- 100.0 °C Elastic modulus of 205 - 207 GPa
- 200.0 °C Elastic modulus of 195 - 199 GPa
- 300.0 °C Elastic modulus of 185 - 192 GPa
- 400.0 °C Elastic modulus of 175 - 184 GPa
- 500.0 °C Elastic modulus of 175 GPa
- 600.0 °C Elastic modulus of 164 GPa
Elongation 20.0 °C Elongation of 12 - 15 %
Poisson's ratio 20.0 °C Poisson's ratio of 0.28 [-]
Reduction of area 20.0 °C Reduction of area of 35 - 45 %
Shear modulus 20.0 °C Shear modulus of 81 GPa
Tensile strength 20.0 °C Tensile strength of 700 - 1100 MPa
Yield strength 20.0 °C Yield strength of 460 - 700 MPa