EN 10263-3 Grade 20MoCr4 annealed to achieve spheroidized carbides and turned
EN 10263-3 Grade 20MoCr4 annealed to achieve spheroidized carbides and turned introduction
The cold-upsettable steel 20 MoCr 5 is suitable for the manufacture of screws and nuts (soft-annealed condition with pre- and/or post treatment) used in automobile, motor and equipment construction and in general engineering. The steel finds additional use, amongst other things, for bevel gears, gear shafts, valve spring plates (for example in case-hardened condition).
Equivalent material: NBN 20MoCr4, BS 805M20, ISO B31, JIS SNCM220, SS 2506-03, UNE F.1523-20MoCr4, ASTM 8620, DIN 1.7321, AFNOR 20MoCr4, BS 20MoCr4, AISI 4118H, AISI 4118, SAE 4118H, SAE 4118, EN 20MoCr4, EN 1.7321, GB/T B10200, GB/T G20CrMo, GB/T 20CrMo, ASTM 4118H, ASTM 4118, UNS H41180, UNS G41180
EN 10263-3 Grade 20MoCr4 annealed to achieve spheroidized carbides and turned general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.83 g/cm³ |
EN 10263-3 Grade 20MoCr4 annealed to achieve spheroidized carbides and turned thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
-100.0 °C |
Coefficient of thermal expansion of 1.05E-5 1/K |
- |
| - |
20.0 °C |
Coefficient of thermal expansion of 1.15E-5 1/K |
- |
| - |
100.0 °C |
Coefficient of thermal expansion of 1.21E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.27E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.32E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.36E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.4E-5 1/K |
- |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.44E-5 1/K |
- |
| Melting point |
- |
Melting point of 1382 - 1529 °C |
Typical for Chromium Molybdenum Steel |
| Specific heat capacity |
-100.0 °C |
Specific heat capacity of 423 J/(kg·K) |
- |
| - |
20.0 °C |
Specific heat capacity of 461 J/(kg·K) |
- |
| - |
100.0 °C |
Specific heat capacity of 479 J/(kg·K) |
- |
| - |
200.0 °C |
Specific heat capacity of 499 J/(kg·K) |
- |
| - |
300.0 °C |
Specific heat capacity of 517 J/(kg·K) |
- |
| - |
400.0 °C |
Specific heat capacity of 536 J/(kg·K) |
- |
| - |
500.0 °C |
Specific heat capacity of 558 J/(kg·K) |
- |
| - |
600.0 °C |
Specific heat capacity of 587 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 41 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 42.7 W/(m·K) |
- |
| - |
200.0 °C |
Thermal conductivity of 42.8 W/(m·K) |
- |
| - |
300.0 °C |
Thermal conductivity of 41.6 W/(m·K) |
- |
| - |
400.0 °C |
Thermal conductivity of 39.9 W/(m·K) |
- |
| - |
500.0 °C |
Thermal conductivity of 37.8 W/(m·K) |
- |
| - |
600.0 °C |
Thermal conductivity of 35.6 W/(m·K) |
- |
| Thermal diffusivity |
20.0 °C |
Thermal diffusivity of 11.4 mm²/s |
- |
| - |
100.0 °C |
Thermal diffusivity of 11 mm²/s |
- |
| - |
200.0 °C |
Thermal diffusivity of 10.3 mm²/s |
- |
| - |
300.0 °C |
Thermal diffusivity of 9.5 mm²/s |
- |
| - |
400.0 °C |
Thermal diffusivity of 8.5 mm²/s |
- |
| - |
500.0 °C |
Thermal diffusivity of 7.3 mm²/s |
- |
| - |
600.0 °C |
Thermal diffusivity of 6 mm²/s |
- |
EN 10263-3 Grade 20MoCr4 annealed to achieve spheroidized carbides and turned chemical
| Property |
Value |
| Carbon |
Carbon of 0.17 - 0.22 % |
| Chromium |
Chromium of 0.3 - 0.6 % |
| Manganese |
Manganese of 0.7 - 1 % |
| Molybdenum |
Molybdenum of 0.4 - 0.5 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 0.4 % |
| Sulfur |
Sulfur of 0.035 % |
EN 10263-3 Grade 20MoCr4 annealed to achieve spheroidized carbides and turned electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 2.54E-7 Ω·m |
| - |
100.0 °C |
Electrical resistivity of 3E-7 Ω·m |
| - |
200.0 °C |
Electrical resistivity of 3.69E-7 Ω·m |
| - |
300.0 °C |
Electrical resistivity of 4.51E-7 Ω·m |
| - |
400.0 °C |
Electrical resistivity of 5.45E-7 Ω·m |
| - |
500.0 °C |
Electrical resistivity of 6.54E-7 Ω·m |
| - |
600.0 °C |
Electrical resistivity of 7.78E-7 Ω·m |
EN 10263-3 Grade 20MoCr4 annealed to achieve spheroidized carbides and turned mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
-100.0 °C |
Elastic modulus of 217 GPa |
- |
| - |
20.0 °C |
Elastic modulus of 212 GPa |
- |
| - |
100.0 °C |
Elastic modulus of 207 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 199 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 192 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 184 GPa |
- |
| - |
500.0 °C |
Elastic modulus of 175 GPa |
- |
| - |
600.0 °C |
Elastic modulus of 164 GPa |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Chromium Molybdenum Steel |
| Reduction of area |
20.0 °C |
Reduction of area of 60 % |
- |
| Tensile strength |
20.0 °C |
Tensile strength of 550 MPa |
- |
Optimize your operations with our efficient steel solutions, designed to enhance productivity and reduce costs.