EN 10263-3 Grade 21NiCrMo2 annealed to achieve spheroidized carbides and turned
EN 10263-3 Grade 21NiCrMo2 annealed to achieve spheroidized carbides and turned introduction
The cold-upsettable steel 21 NiCrMo 2 is suitable for the manufacture of screws and nuts (soft-annealed condition with pre- and/or post treatment) used in automobile, motor and equipment construction and in general engineering. The steel finds additional use, amongst other things, for drive sprockets, gudgeon pins, gear shafts (for example in case-hardened condition).
Equivalent material: NBN 20NiCrMo2, GB 20CrNiMoH, AFNOR 20NCD2, BS 805M20, ISO B41, UNI 20NiCrMo2, JIS SNCM220H, JIS SNCM220, PN 20HNM, UNE F.1222-20NiCrMo2, ASTM 8620, DIN 20NiCrMo2-2, DIN 1.6523, AFNOR 20NiCrMo2-2, BS 21NiCrMo2-2, UNI 20NiCrMo2-2, SS 2506, UNE 20NiCrMo2, AISI 8620, AISI 8617H, AISI 8620H, AISI 8617, SAE 8620, SAE 8617H, SAE 8620H, SAE 8617, JIS SNCM220WCH, JIS SNCM220RCH, JIS 20NiCrMo2, EN 21NiCrMo2, EN 20NiCrMo2-2, EN 1.6523, ISO 20NiCrMo2-2, GOST 20ChGNM, ASTM 8620H, ASTM 8617H, UNS G86200, UNS H86170, UNS H86200, UNS G86170
EN 10263-3 Grade 21NiCrMo2 annealed to achieve spheroidized carbides and turned general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.84 g/cm³ |
EN 10263-3 Grade 21NiCrMo2 annealed to achieve spheroidized carbides and turned thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
-100.0 °C |
Coefficient of thermal expansion of 1.05E-5 1/K |
- |
| - |
20.0 °C |
Coefficient of thermal expansion of 1.15E-5 1/K |
- |
| - |
100.0 °C |
Coefficient of thermal expansion of 1.21E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.27E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.32E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.36E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.4E-5 1/K |
- |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.44E-5 1/K |
- |
| Melting point |
- |
Melting point of 1382 - 1529 °C |
Typical for Nickel Chromium Molybdenum Steel |
| Specific heat capacity |
-100.0 °C |
Specific heat capacity of 423 J/(kg·K) |
- |
| - |
20.0 °C |
Specific heat capacity of 461 J/(kg·K) |
- |
| - |
100.0 °C |
Specific heat capacity of 479 J/(kg·K) |
- |
| - |
200.0 °C |
Specific heat capacity of 499 J/(kg·K) |
- |
| - |
300.0 °C |
Specific heat capacity of 517 J/(kg·K) |
- |
| - |
400.0 °C |
Specific heat capacity of 536 J/(kg·K) |
- |
| - |
500.0 °C |
Specific heat capacity of 558 J/(kg·K) |
- |
| - |
600.0 °C |
Specific heat capacity of 587 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 46.3 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 47.1 W/(m·K) |
- |
| - |
200.0 °C |
Thermal conductivity of 46.2 W/(m·K) |
- |
| - |
300.0 °C |
Thermal conductivity of 44.1 W/(m·K) |
- |
| - |
400.0 °C |
Thermal conductivity of 41.3 W/(m·K) |
- |
| - |
500.0 °C |
Thermal conductivity of 38.6 W/(m·K) |
- |
| - |
600.0 °C |
Thermal conductivity of 35.9 W/(m·K) |
- |
| Thermal diffusivity |
20.0 °C |
Thermal diffusivity of 12.8 mm²/s |
- |
| - |
100.0 °C |
Thermal diffusivity of 12.1 mm²/s |
- |
| - |
200.0 °C |
Thermal diffusivity of 11.1 mm²/s |
- |
| - |
300.0 °C |
Thermal diffusivity of 10 mm²/s |
- |
| - |
400.0 °C |
Thermal diffusivity of 8.8 mm²/s |
- |
| - |
500.0 °C |
Thermal diffusivity of 7.4 mm²/s |
- |
| - |
600.0 °C |
Thermal diffusivity of 4.7 mm²/s |
- |
EN 10263-3 Grade 21NiCrMo2 annealed to achieve spheroidized carbides and turned chemical
| Property |
Value |
| Carbon |
Carbon of 0.17 - 0.23 % |
| Chromium |
Chromium of 0.4 - 0.7 % |
| Manganese |
Manganese of 0.65 - 0.95 % |
| Molybdenum |
Molybdenum of 0.15 - 0.25 % |
| Nickel |
Nickel of 0.4 - 0.7 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 0.4 % |
| Sulfur |
Sulfur of 0.035 % |
EN 10263-3 Grade 21NiCrMo2 annealed to achieve spheroidized carbides and turned electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 2.25E-7 Ω·m |
| - |
100.0 °C |
Electrical resistivity of 2.72E-7 Ω·m |
| - |
200.0 °C |
Electrical resistivity of 3.42E-7 Ω·m |
| - |
300.0 °C |
Electrical resistivity of 4.26E-7 Ω·m |
| - |
400.0 °C |
Electrical resistivity of 5.26E-7 Ω·m |
| - |
500.0 °C |
Electrical resistivity of 6.4E-7 Ω·m |
| - |
600.0 °C |
Electrical resistivity of 7.73E-7 Ω·m |
EN 10263-3 Grade 21NiCrMo2 annealed to achieve spheroidized carbides and turned mechanical
| Property |
Temperature |
Value |
| Elastic modulus |
-100.0 °C |
Elastic modulus of 217 GPa |
| - |
20.0 °C |
Elastic modulus of 212 - 212.78 GPa |
| - |
100.0 °C |
Elastic modulus of 207 GPa |
| - |
200.0 °C |
Elastic modulus of 199 GPa |
| - |
300.0 °C |
Elastic modulus of 192 GPa |
| - |
400.0 °C |
Elastic modulus of 184 GPa |
| - |
500.0 °C |
Elastic modulus of 175 GPa |
| - |
600.0 °C |
Elastic modulus of 164 GPa |
| Poisson's ratio |
20.0 °C |
Poisson's ratio of 0.29 [-] |
| Reduction of area |
20.0 °C |
Reduction of area of 59 % |
| Shear modulus |
20.0 °C |
Shear modulus of 82.8 GPa |
| Tensile strength |
20.0 °C |
Tensile strength of 590 MPa |
Trust our high-quality steel to forge a brighter and stronger future for your projects.
-- Our promise