EN 10222-5 Grade X7CrNiNb18-10 solution annealed (+AT)
EN 10222-5 Grade X7CrNiNb18-10 solution annealed (+AT) introduction
The corrosion resistant material X7CrNiNb18-10, material number 1.4912 is predominantly used for pressure vessel construction.
Equivalent material: GB 07Cr18Ni11Nb, GB S34779, IS 7Cr18Ni11NbH, ASTM A182 Grade F347H, ASTM A965 Grade F347H, ASME SA-182 Grade F347H, UNS S34709, ISO X7CrNiNb18-10, AISI Grade F347H, AISI F347H, DIN 1.4912, AISI 347H, SAE 347H, JIS SUS347H, JIS SUS347HTP, JIS SUS347HTB, JIS SUS347HTF, EN 1.4912, ASTM Grade F347H
EN 10222-5 Grade X7CrNiNb18-10 solution annealed (+AT) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.9 g/cm³ |
EN 10222-5 Grade X7CrNiNb18-10 solution annealed (+AT) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
100.0 °C |
Coefficient of thermal expansion of 1.6E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.65E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.7E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.75E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.8E-5 1/K |
- |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.85E-5 1/K |
- |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
20.0 °C |
Specific heat capacity of 500 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 15 W/(m·K) |
- |
EN 10222-5 Grade X7CrNiNb18-10 solution annealed (+AT) chemical
| Property |
Value |
| Carbon |
Carbon of 0.04 - 0.1 % |
| Chromium |
Chromium of 17 - 19 % |
| Manganese |
Manganese of 2 % |
| Nickel |
Nickel of 9 - 12 % |
| Niobium |
Niobium of 1.2 % |
| Phosphorus |
Phosphorus of 0.05 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.015 % |
EN 10222-5 Grade X7CrNiNb18-10 solution annealed (+AT) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 7.3E-7 Ω·m |
EN 10222-5 Grade X7CrNiNb18-10 solution annealed (+AT) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 200 GPa |
- |
| - |
100.0 °C |
Elastic modulus of 194 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 186 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 179 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 172 GPa |
- |
| - |
500.0 °C |
Elastic modulus of 165 GPa |
- |
| - |
600.0 °C |
Elastic modulus of 155 GPa |
- |
| Elongation |
20.0 °C |
Elongation of 30 - 40 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 510 - 710 MPa |
- |
| Yield strength Rp0.2 |
20.0 °C |
Yield strength Rp0.2 of 205 MPa |
- |
| Yield strength Rp1.0 |
20.0 °C |
Yield strength Rp1.0 of 240 MPa |
- |