EN 10216-5 Grade X6CrNiNb18-10 solution annealed (+AT)
EN 10216-5 Grade X6CrNiNb18-10 solution annealed (+AT) introduction
Material X6CrNiNb18-10 is comparable to X 6 CrNiNb 18 10 acc. to DIN 17440: 1985-07. Its corrosion properties are comparable to 1.4541. The steel is resistant to intercrystalline corrosion also in sensitized condition, but it shows heat-crack susceptibility under certain welding conditions. Widely applicable for welded parts in chemical apparatus engineering, in food and luxury food industry, in film and photo industry as well as for household appliances. The steel is unsuitable for mirror finishing due to its Nb-content.
Equivalent material: GB 0Cr18Ni11Nb, GB 1Cr19Ni11Nb, GB S34771, GB S34778, IS 04Cr19Ni9Nb40, IS TP348, JIS SUS347TB, JIS SUS347HTB, KS STS347TB, UNS S34700, UNS S34800, ASTM 347, ASTM 348, ASME 347, ASME 348, GB 06Cr18Ni11Nb, ISO X7CrNiNb18-11, ASTM A213Type347, ASME SA-213Type347, AISI 347, AISI Type347, DIN 1.4550, DIN X6CrNiNb18-10, DIN X10CrNiNb, AFNOR Z6CNNb18-10, BS 347S17, UNI X6CrNiNb1811, SS 2338, UNE F.3552, UNE F.3524, AISI 347H, SAE 347H, JIS SUS347, JIS SUS347TP, JIS SUS347TPY, JIS SUS347TF, JIS SUS347TKA, JIS SUS347FB, EN 1.4550, ASTM S34709, ASTM Grade F347H, UNS S34709
EN 10216-5 Grade X6CrNiNb18-10 solution annealed (+AT) general
| Property | Temperature | Value |
|---|---|---|
| Density | 20.0 °C | Density of 7.93 g/cm³ |
EN 10216-5 Grade X6CrNiNb18-10 solution annealed (+AT) thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Coefficient of thermal expansion | -100.0 °C | Coefficient of thermal expansion of 1.49E-5 1/K | - |
| - | 20.0 °C | Coefficient of thermal expansion of 1.61E-5 1/K | - |
| - | 100.0 °C | Coefficient of thermal expansion of 1.67E-5 1/K | - |
| - | 200.0 °C | Coefficient of thermal expansion of 1.72E-5 1/K | - |
| - | 300.0 °C | Coefficient of thermal expansion of 1.77E-5 1/K | - |
| - | 400.0 °C | Coefficient of thermal expansion of 1.81E-5 1/K | - |
| - | 425.0 °C | Coefficient of thermal expansion of 1.76E-5 1/K | - |
| - | 485.0 °C | Coefficient of thermal expansion of 1.78E-5 1/K | - |
| - | 500.0 °C | Coefficient of thermal expansion of 1.84E-5 1/K | - |
| - | 540.0 °C | Coefficient of thermal expansion of 1.8E-5 1/K | - |
| - | 595.0 °C | Coefficient of thermal expansion of 1.83E-5 1/K | - |
| - | 600.0 °C | Coefficient of thermal expansion of 1.88E-5 1/K | - |
| - | 650.0 °C | Coefficient of thermal expansion of 1.85E-5 1/K | - |
| - | 700.0 °C | Coefficient of thermal expansion of 1.91E-5 1/K | - |
| - | 705.0 °C | Coefficient of thermal expansion of 1.87E-5 1/K | - |
| - | 800.0 °C | Coefficient of thermal expansion of 1.94E-5 1/K | - |
| - | 900.0 °C | Coefficient of thermal expansion of 1.97E-5 1/K | - |
| - | 1000.0 °C | Coefficient of thermal expansion of 2E-5 1/K | - |
| Melting point | - | Melting point of 1230 - 1480 °C | Typical for Austenitic Stainless Steel |
| Specific heat capacity | -100.0 °C | Specific heat capacity of 440 J/(kg·K) | - |
| - | 20.0 °C | Specific heat capacity of 472 J/(kg·K) | - |
| - | 100.0 °C | Specific heat capacity of 487 J/(kg·K) | - |
| - | 200.0 °C | Specific heat capacity of 503 J/(kg·K) | - |
| - | 300.0 °C | Specific heat capacity of 512 J/(kg·K) | - |
| - | 400.0 °C | Specific heat capacity of 520 J/(kg·K) | - |
| - | 500.0 °C | Specific heat capacity of 530 J/(kg·K) | - |
| - | 600.0 °C | Specific heat capacity of 541 J/(kg·K) | - |
| - | 700.0 °C | Specific heat capacity of 551 J/(kg·K) | - |
| - | 800.0 °C | Specific heat capacity of 559 J/(kg·K) | - |
| - | 900.0 °C | Specific heat capacity of 565 J/(kg·K) | - |
| - | 1000.0 °C | Specific heat capacity of 571 J/(kg·K) | - |
| Thermal conductivity | 20.0 °C | Thermal conductivity of 14.3 W/(m·K) | - |
| - | 100.0 °C | Thermal conductivity of 15.8 W/(m·K) | - |
| - | 200.0 °C | Thermal conductivity of 17.5 W/(m·K) | - |
| - | 300.0 °C | Thermal conductivity of 19 W/(m·K) | - |
| - | 400.0 °C | Thermal conductivity of 20.5 W/(m·K) | - |
| - | 500.0 °C | Thermal conductivity of 21.9 W/(m·K) | - |
| - | 600.0 °C | Thermal conductivity of 23.3 W/(m·K) | - |
| - | 700.0 °C | Thermal conductivity of 24.6 W/(m·K) | - |
| - | 800.0 °C | Thermal conductivity of 26 W/(m·K) | - |
| - | 900.0 °C | Thermal conductivity of 27.4 W/(m·K) | - |
| - | 1000.0 °C | Thermal conductivity of 28.8 W/(m·K) | - |
| Thermal diffusivity | 20.0 °C | Thermal diffusivity of 3.8 mm²/s | - |
| - | 100.0 °C | Thermal diffusivity of 4 mm²/s | - |
| - | 200.0 °C | Thermal diffusivity of 4.2 mm²/s | - |
| - | 300.0 °C | Thermal diffusivity of 4.6 mm²/s | - |
| - | 400.0 °C | Thermal diffusivity of 4.8 mm²/s | - |
| - | 500.0 °C | Thermal diffusivity of 4.9 mm²/s | - |
| - | 600.0 °C | Thermal diffusivity of 5 mm²/s | - |
| - | 700.0 °C | Thermal diffusivity of 5.3 mm²/s | - |
| - | 800.0 °C | Thermal diffusivity of 5.6 mm²/s | - |
| - | 900.0 °C | Thermal diffusivity of 5.9 mm²/s | - |
| - | 1000.0 °C | Thermal diffusivity of 6 mm²/s | - |
EN 10216-5 Grade X6CrNiNb18-10 solution annealed (+AT) chemical
| Property | Value |
|---|---|
| Carbon | Carbon of 0.08 % |
| Chromium | Chromium of 17 - 19 % |
| Manganese | Manganese of 2 % |
| Nickel | Nickel of 9 - 12 % |
| Niobium | Niobium of 1 % |
| Phosphorus | Phosphorus of 0.04 % |
| Silicon | Silicon of 1 % |
| Sulfur | Sulfur of 0.015 % |
EN 10216-5 Grade X6CrNiNb18-10 solution annealed (+AT) electrical
| Property | Temperature | Value |
|---|---|---|
| Electrical resistivity | 20.0 °C | Electrical resistivity of 7.1E-7 Ω·m |
| - | 100.0 °C | Electrical resistivity of 7.76E-7 Ω·m |
| - | 200.0 °C | Electrical resistivity of 8.49E-7 Ω·m |
| - | 300.0 °C | Electrical resistivity of 9.14E-7 Ω·m |
| - | 400.0 °C | Electrical resistivity of 9.71E-7 Ω·m |
| - | 500.0 °C | Electrical resistivity of 1.02E-6 Ω·m |
| - | 600.0 °C | Electrical resistivity of 1.07E-6 Ω·m |
| - | 700.0 °C | Electrical resistivity of 1.1E-6 Ω·m |
| - | 800.0 °C | Electrical resistivity of 1.14E-6 Ω·m |
| - | 900.0 °C | Electrical resistivity of 1.17E-6 Ω·m |
| - | 1000.0 °C | Electrical resistivity of 1.19E-6 Ω·m |
EN 10216-5 Grade X6CrNiNb18-10 solution annealed (+AT) mechanical
| Property | Temperature | Value |
|---|---|---|
| Elastic modulus | -100.0 °C | Elastic modulus of 206 GPa |
| - | 20.0 °C | Elastic modulus of 196 - 199.26 GPa |
| - | 95.0 °C | Elastic modulus of 194.43 GPa |
| - | 100.0 °C | Elastic modulus of 190 GPa |
| - | 150.0 °C | Elastic modulus of 189.61 GPa |
| - | 200.0 °C | Elastic modulus of 182 GPa |
| - | 205.0 °C | Elastic modulus of 184.78 GPa |
| - | 260.0 °C | Elastic modulus of 179.95 GPa |
| - | 300.0 °C | Elastic modulus of 174 GPa |
| - | 315.0 °C | Elastic modulus of 175.13 GPa |
| - | 370.0 °C | Elastic modulus of 170.99 GPa |
| - | 400.0 °C | Elastic modulus of 166 GPa |
| - | 425.0 °C | Elastic modulus of 166.16 GPa |
| - | 485.0 °C | Elastic modulus of 161.34 GPa |
| - | 500.0 °C | Elastic modulus of 158 GPa |
| - | 540.0 °C | Elastic modulus of 157.2 GPa |
| - | 595.0 °C | Elastic modulus of 151.69 GPa |
| - | 600.0 °C | Elastic modulus of 150 GPa |
| - | 650.0 °C | Elastic modulus of 147.54 GPa |
| - | 700.0 °C | Elastic modulus of 142 GPa |
| - | 705.0 °C | Elastic modulus of 142.72 GPa |
| - | 760.0 °C | Elastic modulus of 137.9 GPa |
| - | 800.0 °C | Elastic modulus of 134 GPa |
| - | 815.0 °C | Elastic modulus of 133.76 GPa |
| - | 870.0 °C | Elastic modulus of 128.93 GPa |
| - | 900.0 °C | Elastic modulus of 127 GPa |
| - | 1000.0 °C | Elastic modulus of 120 GPa |
| Elongation | 20.0 °C | Elongation of 35 % |
| Elongation, transverse | 20.0 °C | Elongation, transverse of 30 % |
| Poisson's ratio | 20.0 °C | Poisson's ratio of 0.27 [-] |
| - | 95.0 °C | Poisson's ratio of 0.28 [-] |
| - | 150.0 °C | Poisson's ratio of 0.29 [-] |
| - | 205.0 °C | Poisson's ratio of 0.29 [-] |
| - | 260.0 °C | Poisson's ratio of 0.29 [-] |
| - | 315.0 °C | Poisson's ratio of 0.3 [-] |
| - | 370.0 °C | Poisson's ratio of 0.31 [-] |
| - | 425.0 °C | Poisson's ratio of 0.31 [-] |
| - | 485.0 °C | Poisson's ratio of 0.32 [-] |
| - | 540.0 °C | Poisson's ratio of 0.33 [-] |
| - | 595.0 °C | Poisson's ratio of 0.33 [-] |
| - | 650.0 °C | Poisson's ratio of 0.32 [-] |
| - | 705.0 °C | Poisson's ratio of 0.33 [-] |
| - | 760.0 °C | Poisson's ratio of 0.35 [-] |
| - | 815.0 °C | Poisson's ratio of 0.35 [-] |
| - | 870.0 °C | Poisson's ratio of 0.36 [-] |
| Shear modulus | 20.0 °C | Shear modulus of 78.6 GPa |
| - | 95.0 °C | Shear modulus of 75.84 GPa |
| - | 150.0 °C | Shear modulus of 73.77 GPa |
| - | 205.0 °C | Shear modulus of 71.71 GPa |
| - | 260.0 °C | Shear modulus of 69.64 GPa |
| - | 315.0 °C | Shear modulus of 67.57 GPa |
| - | 370.0 °C | Shear modulus of 65.5 GPa |
| - | 425.0 °C | Shear modulus of 63.43 GPa |
| - | 485.0 °C | Shear modulus of 61.36 GPa |
| - | 540.0 °C | Shear modulus of 59.3 GPa |
| - | 595.0 °C | Shear modulus of 57.23 GPa |
| - | 650.0 °C | Shear modulus of 55.85 GPa |
| - | 705.0 °C | Shear modulus of 53.78 GPa |
| - | 760.0 °C | Shear modulus of 51.11 GPa |
| - | 815.0 °C | Shear modulus of 49.64 GPa |
| - | 870.0 °C | Shear modulus of 47.57 GPa |
| Tensile strength | 20.0 °C | Tensile strength of 510 - 740 MPa |
| Tensile strength, transverse | 20.0 °C | Tensile strength, transverse of 510 - 740 MPa |
| Yield strength Rp0.2 | 20.0 °C | Yield strength Rp0.2 of 205 MPa |
| - | 50.0 °C | Yield strength Rp0.2 of 195 MPa |
| - | 100.0 °C | Yield strength Rp0.2 of 175 MPa |
| - | 150.0 °C | Yield strength Rp0.2 of 165 MPa |
| - | 200.0 °C | Yield strength Rp0.2 of 155 MPa |
| - | 250.0 °C | Yield strength Rp0.2 of 145 MPa |
| - | 300.0 °C | Yield strength Rp0.2 of 136 MPa |
| - | 350.0 °C | Yield strength Rp0.2 of 130 MPa |
| - | 400.0 °C | Yield strength Rp0.2 of 125 MPa |
| - | 450.0 °C | Yield strength Rp0.2 of 121 MPa |
| - | 500.0 °C | Yield strength Rp0.2 of 119 MPa |
| - | 550.0 °C | Yield strength Rp0.2 of 118 MPa |
| Yield strength Rp0.2, transverse | 20.0 °C | Yield strength Rp0.2, transverse of 205 MPa |
| Yield strength Rp1.0 | 20.0 °C | Yield strength Rp1.0 of 240 MPa |
| - | 50.0 °C | Yield strength Rp1.0 of 232 MPa |
| - | 100.0 °C | Yield strength Rp1.0 of 210 MPa |
| - | 150.0 °C | Yield strength Rp1.0 of 195 MPa |
| - | 200.0 °C | Yield strength Rp1.0 of 185 MPa |
| - | 250.0 °C | Yield strength Rp1.0 of 175 MPa |
| - | 300.0 °C | Yield strength Rp1.0 of 167 MPa |
| - | 350.0 °C | Yield strength Rp1.0 of 161 MPa |
| - | 400.0 °C | Yield strength Rp1.0 of 156 MPa |
| - | 450.0 °C | Yield strength Rp1.0 of 152 MPa |
| - | 500.0 °C | Yield strength Rp1.0 of 149 MPa |
| - | 550.0 °C | Yield strength Rp1.0 of 147 MPa |
| Yield strength Rp1.0, transverse | 20.0 °C | Yield strength Rp1.0, transverse of 240 MPa |
Our state-of-the-art facilities ensure precision manufacturing and impeccable finishes.
-- Our promise
Similar or equivalent steel materials
- UGI®347H – UGI®4550
- Sandvik 8R40
- Sandvik 6R44
- DIN 17440 Grade X6CrNiNb18-10 solution heat-treated and quenched
- DIN 17440 Grade X6CrNiNb18-10 quenched (+Q)
- EN 10272 Grade X6CrNiNb18-10 solution annealed (+AT)
- EN 10028-7 Grade X6CrNiNb18-10 solution annealed (+AT)
- EN 10217-7 Grade X6CrNiNb18-10 solution annealed (+AT)
- EN 10250-4 Grade X6CrNiNb18-10 solution annealed (+AT)
- EN 10222-5 Grade X6CrNiNb18-10 solution annealed (+AT)