EN 10222-5 Grade X2CrNiMoN17-11-2 solution annealed (+AT)
EN 10222-5 Grade X2CrNiMoN17-11-2 solution annealed (+AT) introduction
Trademark X2CrNiMoN17-11-2 is a fully austenitic steel which shows higher strength and structural stability owing to N-addition. To the comparable DIN-make X 2 CrNiMoN 17 12 2 acc. to DIN 17440 : 1985-07 applies: increased pitting index by N-addition. Application in chemical apparatus engineering for pressure vessels, in cellulose, color, oil, soap and textile industry, in breweries and dairies. The steel is suitable for mirror finishing and corrosion resistant to selective attack particularly in welded condition. The material shows resistance to intercrystalline corrosion also in sensitized condition.
Equivalent material: GB 022Cr17Ni12Mo2N, GB S31653, JIS SUSF316LN, KS STSF316LN, ASTM A965 Grade F316LN, UNS S31653, ISO X2CrNiMoN17-12, ASTM Grade F316LN, ASTM F316LN, DIN X2CrNiMoN17-12-2, DIN 1.4406, DIN X2CrNiMoN17-11-2, AFNOR Z3CND17-11Az, BS 316S61, BS 316S13, UNE F.3542, AISI 316LN, SAE 316LN, JIS SUS316LN, EN 1.4406
EN 10222-5 Grade X2CrNiMoN17-11-2 solution annealed (+AT) general
| Property |
Temperature |
Value |
| Density |
20.0 °C |
Density of 7.96 - 8 g/cm³ |
EN 10222-5 Grade X2CrNiMoN17-11-2 solution annealed (+AT) thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
-100.0 °C |
Coefficient of thermal expansion of 1.49E-5 1/K |
- |
| - |
20.0 °C |
Coefficient of thermal expansion of 1.61E-5 1/K |
- |
| - |
100.0 °C |
Coefficient of thermal expansion of 1.6E-5 - 1.67E-5 1/K |
- |
| - |
200.0 °C |
Coefficient of thermal expansion of 1.65E-5 - 1.72E-5 1/K |
- |
| - |
300.0 °C |
Coefficient of thermal expansion of 1.7E-5 - 1.77E-5 1/K |
- |
| - |
400.0 °C |
Coefficient of thermal expansion of 1.75E-5 - 1.81E-5 1/K |
- |
| - |
500.0 °C |
Coefficient of thermal expansion of 1.8E-5 - 1.84E-5 1/K |
- |
| - |
600.0 °C |
Coefficient of thermal expansion of 1.88E-5 1/K |
- |
| - |
700.0 °C |
Coefficient of thermal expansion of 1.91E-5 1/K |
- |
| - |
800.0 °C |
Coefficient of thermal expansion of 1.94E-5 1/K |
- |
| - |
900.0 °C |
Coefficient of thermal expansion of 1.97E-5 1/K |
- |
| - |
1000.0 °C |
Coefficient of thermal expansion of 2E-5 1/K |
- |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
-100.0 °C |
Specific heat capacity of 440 J/(kg·K) |
- |
| - |
20.0 °C |
Specific heat capacity of 472 - 500 J/(kg·K) |
- |
| - |
100.0 °C |
Specific heat capacity of 487 J/(kg·K) |
- |
| - |
200.0 °C |
Specific heat capacity of 503 J/(kg·K) |
- |
| - |
300.0 °C |
Specific heat capacity of 512 J/(kg·K) |
- |
| - |
400.0 °C |
Specific heat capacity of 520 J/(kg·K) |
- |
| - |
500.0 °C |
Specific heat capacity of 530 J/(kg·K) |
- |
| - |
600.0 °C |
Specific heat capacity of 541 J/(kg·K) |
- |
| - |
700.0 °C |
Specific heat capacity of 551 J/(kg·K) |
- |
| - |
800.0 °C |
Specific heat capacity of 559 J/(kg·K) |
- |
| - |
900.0 °C |
Specific heat capacity of 565 J/(kg·K) |
- |
| - |
1000.0 °C |
Specific heat capacity of 571 J/(kg·K) |
- |
| Thermal conductivity |
20.0 °C |
Thermal conductivity of 13.3 - 15 W/(m·K) |
- |
| - |
100.0 °C |
Thermal conductivity of 14.9 W/(m·K) |
- |
| - |
200.0 °C |
Thermal conductivity of 16.5 W/(m·K) |
- |
| - |
300.0 °C |
Thermal conductivity of 18.1 W/(m·K) |
- |
| - |
400.0 °C |
Thermal conductivity of 19.5 W/(m·K) |
- |
| - |
500.0 °C |
Thermal conductivity of 21 W/(m·K) |
- |
| - |
600.0 °C |
Thermal conductivity of 22.4 W/(m·K) |
- |
| - |
700.0 °C |
Thermal conductivity of 23.8 W/(m·K) |
- |
| - |
800.0 °C |
Thermal conductivity of 25.2 W/(m·K) |
- |
| Thermal diffusivity |
20.0 °C |
Thermal diffusivity of 3.5 mm²/s |
- |
| - |
100.0 °C |
Thermal diffusivity of 3.8 mm²/s |
- |
| - |
200.0 °C |
Thermal diffusivity of 4 mm²/s |
- |
| - |
300.0 °C |
Thermal diffusivity of 4.3 mm²/s |
- |
| - |
400.0 °C |
Thermal diffusivity of 4.5 mm²/s |
- |
| - |
500.0 °C |
Thermal diffusivity of 4.7 mm²/s |
- |
| - |
600.0 °C |
Thermal diffusivity of 4.8 mm²/s |
- |
| - |
700.0 °C |
Thermal diffusivity of 5.1 mm²/s |
- |
| - |
800.0 °C |
Thermal diffusivity of 5.4 mm²/s |
- |
EN 10222-5 Grade X2CrNiMoN17-11-2 solution annealed (+AT) chemical
| Property |
Value |
| Carbon |
Carbon of 0.03 % |
| Chromium |
Chromium of 16.5 - 18.5 % |
| Manganese |
Manganese of 2 % |
| Molybdenum |
Molybdenum of 2 - 2.5 % |
| Nickel |
Nickel of 10 - 12.5 % |
| Nitrogen |
Nitrogen of 0.12 - 0.22 % |
| Phosphorus |
Phosphorus of 0.05 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.015 % |
EN 10222-5 Grade X2CrNiMoN17-11-2 solution annealed (+AT) electrical
| Property |
Temperature |
Value |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 7.91E-7 Ω·m |
| - |
100.0 °C |
Electrical resistivity of 8.45E-7 Ω·m |
| - |
200.0 °C |
Electrical resistivity of 9.19E-7 Ω·m |
| - |
300.0 °C |
Electrical resistivity of 9.77E-7 Ω·m |
| - |
400.0 °C |
Electrical resistivity of 1.03E-6 Ω·m |
| - |
500.0 °C |
Electrical resistivity of 1.08E-6 Ω·m |
| - |
600.0 °C |
Electrical resistivity of 1.12E-6 Ω·m |
| - |
700.0 °C |
Electrical resistivity of 1.15E-6 Ω·m |
| - |
800.0 °C |
Electrical resistivity of 1.18E-6 Ω·m |
EN 10222-5 Grade X2CrNiMoN17-11-2 solution annealed (+AT) mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
-100.0 °C |
Elastic modulus of 206 GPa |
- |
| - |
20.0 °C |
Elastic modulus of 196 - 200 GPa |
- |
| - |
100.0 °C |
Elastic modulus of 190 - 194 GPa |
- |
| - |
200.0 °C |
Elastic modulus of 182 - 186 GPa |
- |
| - |
300.0 °C |
Elastic modulus of 174 - 179 GPa |
- |
| - |
400.0 °C |
Elastic modulus of 166 - 172 GPa |
- |
| - |
500.0 °C |
Elastic modulus of 158 - 165 GPa |
- |
| - |
600.0 °C |
Elastic modulus of 150 GPa |
- |
| - |
700.0 °C |
Elastic modulus of 142 GPa |
- |
| - |
800.0 °C |
Elastic modulus of 134 GPa |
- |
| - |
900.0 °C |
Elastic modulus of 127 GPa |
- |
| - |
1000.0 °C |
Elastic modulus of 120 GPa |
- |
| Elongation |
20.0 °C |
Elongation of 35 - 45 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 580 - 780 MPa |
- |
| Yield strength Rp0.2 |
20.0 °C |
Yield strength Rp0.2 of 280 MPa |
- |
| Yield strength Rp1.0 |
20.0 °C |
Yield strength Rp1.0 of 315 MPa |
- |
Simplify your procurement process with our comprehensive range of steel products.